Sulfide solid electrolyte material, sulfide glass, solid state lithium battery, and method for producing sulfide solid electrolyte material

1. A sulfide solid electrolyte material comprising

an ion conductor having Li, P and S, and having a PS 4 3− structure as a main component of an anion structure,

LiI, and

at least one of LiBr and LiCl,

wherein the sulfide solid electrolyte material contains a high Li ion conducting phase having peaks at 2θ=20.2° and 23.6°, does not contain low Li ion conducting phase having peaks at 2θ=21.0° and 28.0° in an X-ray diffraction measurement using a CuKα ray, and has a half width of the peak at 2θ=20.2° of 0.51° or less.

2. The sulfide solid electrolyte material according to claim 1 , comprising the LiBr,

wherein LiBr/(LiI+LiBr) is in the range of 25 mol % to 50 mol %.

3. The sulfide solid electrolyte material according to claim 1 , comprising the LiCl,

wherein LiCl/(LiI+LiCl) is in the range of 15 mol % to 50 mol %.

4. The sulfide solid electrolyte material according to claim 1 , using a raw material composition which contains Li 2 S, P 2 S 5 , LiI, and at least one of LiBr and LiCl,

wherein Li 2 S/(Li 2 S+P 2 S 5 ) is in the range of 76 mol % to 78 mol %.

5. A sulfide glass, the sulfide glass being used for the sulfide solid electrolyte material according to claim 1 ,

wherein an exothermic peak of the high Li ion conducting phase (c1) and an exothermic peak of the low Li ion conducting phase (cx) are observed by differential thermal analysis, and the sulfide glass satisfies T cx −T c1 ≥55° C. when temperature of the exothermic peak of the c1 is T c1 and temperature of the exothermic peak of the cx is T cx in differential thermal analysis, and

the sulfide solid electrolyte material may be obtained by a heat treatment.

6. A sulfide glass, the sulfide glass being used for the sulfide solid electrolyte material according to claim 1 , comprising: the ion conductor; the LiI; and the LiBr,

wherein LiBr/(LiI+LiBr) is in the range of 25 mol % to 50 mol %,

an exothermic peak of the high Li ion conducting phase (c1) and an exothermic peak of the low Li ion conducting phase (cx) are observed by differential thermal analysis, and the sulfide glass satisfies T cx −T c1 ≥55° C. when temperature of the exothermic peak of the c1 is T c1 and temperature of the exothermic peak of the cx is T cx in differential thermal analysis, and

the sulfide solid electrolyte material may be obtained by a heat treatment.

7. A solid state lithium battery comprising: a cathode active material layer containing a cathode active material; an anode active material layer containing an anode active material; and a solid electrolyte layer formed between the cathode active material layer and the anode active material layer,

wherein at least one of the cathode active material layer, the anode active material layer, and the solid electrolyte layer contains the sulfide solid electrolyte material according to claim 1 .

8. A method for producing a sulfide solid electrolyte material according to claim 1 , the method comprising steps of:

an amorphizing step of obtaining a sulfide glass by amorphization of a raw material composition that contains Li 2 S, P 2 S 5 , LiI, and at least one of LiBr and LiCl; and

a heat treatment step of heating the sulfide glass,

wherein the method uses the sulfide glass in which an exothermic peak of the high Li ion conducting phase (c1) and an exothermic peak of the low Li ion conducting phase (cx) are observed by differential thermal analysis;

the sulfide glass satisfies T cx −T c1 ≥55° C. when temperature of the exothermic peak of the c1 is T c1 and temperature of the exothermic peak of the cx is T cx in differential thermal analysis; and

the heat treatment is performed from (T cx −50)° C. to (T c1 −10)° C. when the treatment time is less than 10 hours, and heat treatment is performed from (T c1 +5)° C. to (T c1 −20)° C. when the treatment time is 10 hours or more.

9. The sulfide solid electrolyte material according to claim 1 , wherein a peak of Li 2 S is not observed in an X-ray diffraction measurement.

10. The sulfide solid electrolyte material according to claim 1 produced from a method comprising:

an amorphizing step of obtaining a sulfide glass by amorphization of a raw material composition that contains Li 2 S, P 2 S 5 , LiI, and at least one of LiBr and LiCl; and

a heat treatment step of heating the sulfide glass,

wherein the method uses the sulfide glass in which an exothermic peak of the high Li ion conducting phase (c1) and an exothermic peak of the low Li ion conducting phase (cx) are observed by differential thermal analysis;

the sulfide glass satisfies T cx −T c1 ≥55° C. when temperature of the exothermic peak of the c1 is T c1 and temperature of the exothermic peak of the cx is T cx in differential thermal analysis; and

the heat treatment is performed from (T cx −50)° C. to (T c1 −10)° C. when the treatment time is less than 10 hours, and heat treatment is performed from (T c1 +5)° C. to (T c1 −20)° C. when the treatment time is 10 hours or more.

11. The sulfide solid electrolyte material according to claim 1 , wherein the high Li ion conducting phase further comprises at least one peak at 2θ=29.4°, 37.8°, 41.1°, and 47.0°.

12. The sulfide solid electrolyte material according to claim 1 , wherein the high Li ion conducting phase further comprises peaks at 2θ=29.4°, 37.8°, 41.1°, and 47.0°.

13. The sulfide solid electrolyte material according to claim 1 , wherein the sulfide solid electrolyte material does not substantially contain Li 2 S.

14. The sulfide solid electrolyte material according to claim 1 , wherein the sulfide solid electrolyte material does not substantially contain cross-linking sulfur.

15. The sulfide solid electrolyte material according to claim 2 , wherein the sulfide solid electrolyte material has a composition of aLiX.(1−a)(bLi 2 S.(1−b)P 2 S 5 ), wherein “LiX” represents LiI and LiBr, “a” satisfies 0.1≤a≤0.3, and “b” satisfies 0.74≤b≤0.76.

16. The sulfide solid electrolyte material according to claim 15 , wherein “a” satisfies 0.15≤a≤0.25.

17. The sulfide solid electrolyte material according to claim 3 , wherein LiCl/(LiI+LiCl) is in the range of 25 mol % to 50 mol %, and

the sulfide solid electrolyte material has a composition of aLiX.(1−a)(bLi 2 S.(1−b)P 2 S 5 ), wherein “LiX” represents LiI and LiCl, “a” satisfies 0.1≤a≤0.3, and “b” satisfies 0.74≤b≤0.76.