Abrasive grains on basis of eutectic alumina zirconia

1. Abrasive grains based on Al 2 O 3 and ZrO 2 fused in an electric arc furnace and having a weight content of:

Al 2 O 3 between 52% and 62% by weight;

ZrO 2 and HfO 2 between 35% and 45% by weight, with at least 60% by weight, based on the total weight content of ZrO 2 , being present in the tetragonal and/or cubic high temperature modifications of ZrO 2 ;

Si-compounds between 0.2% and 0.7% by weight, expressed as SiO 2 ;

carbon between 0.03% and 0.5% by weight;

additives between 0.5% and 10% by weight; and

raw-material-based impurities of less than 3% by weight,

wherein the abrasive grains are characterized in that after quenching the melt, crushing the solidified fused product and screening it into grit sizes, the abrasive grains are heat treated in air between 350° C. and 700° C. for a time period of one to six hours.

2. The abrasive grains according to claim 1 , characterized in that the additives are selected from the group consisting of reduced Ti-compounds, Y 2 O 3 , MgO, CaO, and/or mixtures thereof.

3. The abrasive grains according to claim 1 , characterized in that the abrasive grains are heat treated in air between 400° C. and 600° C. for a time period of two to four hours.

4. The abrasive grains according to claim 1 , characterized in that the additives comprise at least one reduced titanium compound in the form of oxides, suboxides, carbides, oxycarbides, oxycarbonitrides, and/or silicides.

5. The abrasive grains according to claim 1 , characterized in that between 65% and 85% by weight of ZrO 2 , based on the total weight content of ZrO 2 , are present in the tetragonal and/or cubic high-temperature modifications.

6. The abrasive grains according to claim 1 , characterized in that the abrasive grains have an improved grain fracture strength (CFF) according to Vollstaedt of at least 95 N.

7. The abrasive grains according to claim 1 , characterized in that the abrasive grains have a minimized micro grit decomposition (MKZ) of less than 6%.

8. The abrasive grains according to claim 1 , characterized in that the additives comprise a reduced titanium compound in the form of oxides, suboxides, carbides, oxycarbides, oxycarbonitrides, and/or silicides, whereby between 60% and 80% by weight of ZrO 2 , based on the total weight content of ZrO 2 , are present in the tetragonal and/or cubic high-temperature modifications, and whereby the abrasive grains have an improved grain fracture strength (CFF) according to Vollstaedt of at least 95 N.

9. A method for producing fused abrasive grains according to claim 1 , the method comprising:

mixing raw materials to produce abrasive grains having the following chemical composition:

a) Al 2 O 3 between 52% and 62% by weight;

b) ZrO 2 and HfO 2 between 35% and 45% by weight, with at least 60% by weight of ZrO 2 , based on the total weight content of ZrO 2 , being present in tetragonal and/or cubic high-temperature modification;

c) Si-compounds between 0.2% and 0.7% by weight expressed as SiO 2 ;

d) carbon between 0.03% and 0.5% by weight;

e) additives between 0.5% and 10% by weight; and

f) raw-material-based impurities of less than 3% by weight;

fusing the mixture in an electric arc furnace;

quenching the fused mixture to obtain a solidified product;

crushing the solidified product and subsequently screening the crushed solidified product to obtain abrasive grains; and

heat treating the abrasive grains at a temperature between 350° C. and 700° C. in air for a time period of one to six hours.