Electrolyte solution and method for producing same, continuously dissolving facility, electrolyte membrane, electrode catalyst layer, membrane electrode assembly and fuel cell
A method for producing an electrolyte solution including a supply step of continuously supplying an emulsion based a polymer electrolyte and a solvent into a dissolution facility, and a dissolution step of continuously dissolving the polymer electrolyte in the solvent by heating the interior of the dissolution facility to obtain the electrolyte solution.
1. A method for producing an electrolyte solution, comprising:
continuously supplying a polymer emulsion that is itself produced by emulsion polymerization and comprising a polymer electrolyte and a solvent into a dissolution facility;
continuously dissolving the polymer electrolyte in the solvent by heating an interior of the dissolution facility to obtain the electrolyte solution, wherein the solvent contains 80 to 100 mass % of water and 0 to 20 mass % of an alcohol; and
continuously discharging the electrolyte solution out of the dissolution facility through a back pressure regulating valve while maintaining a pressurized condition within the dissolution facility;
wherein a heating temperature of the interior of the dissolution facility is from 50° C. to 500° C.; and
wherein the polymer electrolyte contains a fluorine-based polymer electrolyte.
2. The method for producing the electrolyte solution according to claim 1 , wherein a heating temperature of the interior of the dissolution facility is from 150° C. to 350° C.
3. The method for producing the electrolyte solution according to claim 1 , wherein, in the continuously dissolving, a heating temperature of the interior of the dissolution facility is from 150° C. to 290° C.
4. The method for producing the electrolyte solution according to claim 1 , wherein, in the continuously dissolving, a pressure within the dissolution facility exceeds vapor pressure of the solvent at the heating temperature of the dissolution facility.
5. The method for producing the electrolyte solution according to claim 1 , further comprising, after the continuously dissolving, cooling the electrolyte solution while maintaining a pressure exceeding the vapor pressure of the solvent at the heating temperature of the interior of the dissolution facility.
6. The method for producing the electrolyte solution according to claim 1 , wherein the dissolution facility is a tube.
7. The method for producing the electrolyte solution according to claim 1 , wherein
the fluorine-based polymer electrolyte has an average particle diameter of 10 nm or more and less than 500 nm, and
the fluorine-based polymer electrolyte contains a —SO 3 X group where X is an alkali metal, an alkaline-earth metal or NR 1 R 2 R 3 R 4 where R 1 ,R 2 ,R 3 and R 4 are each independently an alkyl group having 1 to 3 carbon atoms or hydrogen.