Vented twin-screw kneading extrusion apparatus and extrusion method
According to the present invention, devolatilization of a synthetic resin formed from a polymer or synthetic rubber can be improved and the synthetic resin can be foamed at a low temperature by injecting a devolatilization agent through a devolatilization agent injection nozzle provided in a downstream end segment cylinder of a cylinder assembly. In a vented twin-screw kneading extrusion apparatus and extrusion method according to the present invention, a devolatilization agent, which is injected through a downstream end devolatilization agent injection nozzle ( 7 c ) provided on a downstream end segment cylinder constituted by a segment cylinder ( 1 g ) positioned on a downstream end of a cylinder assembly ( 1 ), is dispersed in molten resin in the downstream end segment cylinder ( 1 g ) and kneaded by a downstream end kneading portion ( 6 c ) such that the molten resin is foamed by the devolatilization agent and then extruded.
1. A vented twin-screw kneading extrusion method for discharging organic volatile matter contained in molten resin, the molten resin being obtained by melting and kneading a synthetic resin raw material ( 11 ) that is supplied through a raw material supply port ( 3 ) on an upstream side of a cylinder ( 1 ) constituted by a multiple segment cylinders ( 1 a to 1 g ) and is formed from synthetic rubber or from two or more types of polymer including synthetic rubber, to the outside through a vent port ( 4 a , 4 b ) in the cylinder ( 1 ), and extruding the molten resin from a die ( 8 ) provided on a downstream end of the cylinder ( 1 ),
characterized in that a devolatilization agent, which is injected through a downstream end devolatilization agent injection nozzle ( 7 c ) provided on a downstream end segment cylinder constituted by a segment cylinder ( 1 g ) positioned on a downstream end of the cylinder assembly ( 1 ), is dispersed in the molten resin in the downstream end segment cylinder ( 1 g ) and kneaded by a downstream end kneading portion ( 6 c ) such that the molten resin is foamed by the devolatilization agent and then extruded.
2. The vented twin-screw kneading extrusion method according to claim 1 , characterized in that a multiple devolatilization agent injection nozzles ( 7 a , 7 b ), a multiple vent ports ( 4 a , 4 b ), and a multiple kneading portions ( 6 a , 6 b ) are provided between the raw material supply port ( 3 ) and the downstream end segment cylinder ( 1 g ) of the cylinder assembly ( 1 ).
3. The vented twin-screw kneading extrusion method according to claim 2 , characterized in that one of water, nitrogen, and carbon dioxide is used as the devolatilization agent.
4. The vented twin-screw kneading extrusion method according to claim 2 , characterized in that a cylinder temperature of the downstream end segment cylinder ( 1 g ) is set to be equal to or higher than a boiling point of the devolatilization agent and lower than a limit heat resistance temperature of the synthetic rubber.
5. The vented twin-screw kneading extrusion method according to claim 2 , characterized in that the devolatilization agent is injected at a ratio of 1.0% to 15% relative to the molten resin, and
a back pressure on an upstream side of the die ( 8 ) equals or exceeds a vapor pressure of the devolatilization agent at the limit heat resistance temperature of the synthetic rubber.
6. The vented twin-screw kneading extrusion method according to claim 2 , characterized in that the synthetic resin raw material is formed from a mixture of synthetic rubber and an organic solvent, and
the devolatilization agent is formed from water.
7. The vented twin-screw kneading extrusion method according to claim 2 , characterized in that the die ( 8 ) is constituted by a die having a pressure adjustment mechanism.
8. The vented twin-screw kneading extrusion method according to claim 1 , characterized in that one of water, nitrogen, and carbon dioxide is used as the devolatilization agent.
9. The vented twin-screw kneading extrusion method according to claim 8 , characterized in that a cylinder temperature of the downstream end segment cylinder ( 1 g ) is set to be equal to or higher than a boiling point of the devolatilization agent and lower than a limit heat resistance temperature of the synthetic rubber.
10. The vented twin-screw kneading extrusion method according to claim 8 , characterized in that the devolatilization agent is injected at a ratio of 1.0% to 15% relative to the molten resin, and
a back pressure on an upstream side of the die ( 8 ) equals or exceeds a vapor pressure of the devolatilization agent at the limit heat resistance temperature of the synthetic rubber.
11. The vented twin-screw kneading extrusion method according to claim 8 , characterized in that the die ( 8 ) is constituted by a die having a pressure adjustment mechanism.
12. The vented twin-screw kneading extrusion method according to claim 1 , characterized in that a cylinder temperature of the downstream end segment cylinder ( 1 g ) is set to be equal to or higher than a boiling point of the devolatilization agent and lower than a limit heat resistance temperature of the synthetic rubber.
13. The vented twin-screw kneading extrusion method according to claim 12 , characterized in that the synthetic resin raw material is formed from a mixture of synthetic rubber and an organic solvent, and
the devolatilization agent is formed from water.
14. The vented twin-screw kneading extrusion method according to claim 12 , characterized in that the die ( 8 ) is constituted by a die having a pressure adjustment mechanism.
15. The vented twin-screw kneading extrusion method according to claim 1 , characterized in that the devolatilization agent is injected at a ratio of 1.0% to 15% relative to the molten resin, and
a back pressure on an upstream side of the die ( 8 ) equals or exceeds a vapor pressure of the devolatilization agent at the limit heat resistance temperature of the synthetic rubber.
16. The vented twin-screw kneading extrusion method according to claim 15 , characterized in that the synthetic resin raw material is formed from a mixture of synthetic rubber and an organic solvent, and
the devolatilization agent is formed from water.
17. The vented twin-screw kneading extrusion method according to claim 15 , characterized in that the die ( 8 ) is constituted by a die having a pressure adjustment mechanism.
18. The vented twin-screw kneading extrusion method according to claim 1 , characterized in that the synthetic resin raw material is formed from a mixture of synthetic rubber and an organic solvent, and
the devolatilization agent is formed from water.
19. The vented twin-screw kneading extrusion method according to claim 18 , characterized in that the die ( 8 ) is constituted by a die having a pressure adjustment mechanism.
20. The vented twin-screw kneading extrusion method according to claim 1 , characterized in that the die ( 8 ) is constituted by a die having a pressure adjustment mechanism.