Foldable paper-based substrates coated with water-based coatings and process for coating foldable paper-based substrates
A foldable paper-based substrate coated with primer coat and top coat. Primer coat comprises a wax-free aqueous dispersion characterized in that a dry film thereof has a flexibility of at least 1 100% for a film thickness from about 1.0 to about 2.5 mm. Top coat is blocking resistant and comprises an aqueous dispersion of a polymer providing water resistance, grease or oil resistance, heat resistance, odor barrier, moisture barrier and/or heat sealability to the paper-based product. The top coat aqueous dispersion is characterized in that a dry film thereof has a flexibility of at least 570% for a film thickness from about 1.5 to about 2.5 mm. A process for preparing the coated foldable paper-based substrate comprises applying the primer coat to the surface of the paper-based substrate, applying the top coat and drying the coats. The primer coat may be dried before application of the top coat.
1. A repulpable foldable paper-based substrate coated on at least one surface with:
a primer layer formed from a primer coat comprising a wax-free aqueous dispersion of a styrene-acrylate copolymer, styrene-acrylonitrile copolymer, styrene-butadiene copolymer, styrene-acrylonitrile-acrylate copolymer or any mixture of these copolymers, said wax-free aqueous dispersion being characterized in that a dry film thereof has a flexibility measured as the percentage of elongation-to-break of at least 1100% for a film thickness from about 1.0 to about 2.5 mm, and
a top layer formed from a top coat comprising an aqueous dispersion of a polymer or copolymer capable of providing at least one of water resistance, grease or oil resistance, heat resistance, an odor barrier, a moisture barrier, or heat sealability to the coated paper-based substrate, wherein said top layer is blocking resistant and said top coat aqueous dispersion is characterized in that a dry film thereof has a flexibility measured as the percentage of elongation-to-break of at least 570% for a film thickness from about 1.5 to about 2.5 mm,
wherein the primer coat has a viscosity from about 4500 cP to about 10000 cP, the top coat has a viscosity from about 40 cP to about 10000 cP, the viscosity being measured on a Brookfield viscometer at 20 rpm with a spindle 3 , and the primer layer has a thickness from about 10 μm to about 15 μm.
2. The foldable paper-based substrate of claim 1 , wherein the primer coat aqueous dispersion is characterized in that the dry film thereof has a flexibility of at least 1350% for a film thickness from about 1.5 to about 2 mm and the top coat aqueous dispersion is characterized in that the dry film thereof has a flexibility of at least 600% for a film thickness from about 1.6 to about 1.7 mm.
3. The foldable paper-based substrate of claim 1 , wherein the primer coat aqueous dispersion is characterized in that the dry film thereof has a flexibility of at least 1500% for a film thickness from about 1.6 to about 1.7 mm and the top coat aqueous dispersion is characterized in that the dry film thereof has a flexibility of at least 600% for a film thickness from about 1.6 to about 1.7 mm.
4. The foldable paper-based substrate of claim 1 , wherein the primer coat has a solids content from about 30 wt % to about 70 wt % and the top coat has a solids content from about 10 wt % to about 70 wt %.
5. The foldable paper-based substrate of claim 1 , wherein the primer coat has a solids content from about 45 wt % to about 55 wt % and the top coat has a solids content from about 20 wt % to about 40 wt %.
6. The foldable paper-based substrate of claim 1 , wherein the primer coat comprises a copolymer of n-butylacrylate, styrene and acrylonitrile.
7. The foldable paper-based substrate of claim 1 , wherein the top coat comprises an acrylic based polymer or copolymer, a styrene-butadiene copolymer, a styrene-acrylate copolymer, a styrene-acrylonitrile copolymer, a styrene-acrylonitrile-acrylate copolymer, a polyurethane, a polyvinylalcohol, a polyvinylacetate, a dextrin, a modified starch, an asphalt emulsion, corn starch, polyethylene, nylon, polypropylene, a polyhydroxyalkanoate, or any mixtures thereof.
8. The foldable paper-based substrate of claim 1 , wherein the top coat is substantially free of mineral charges and is wax free.
9. The foldable paper-based substrate of claim 1 , wherein the aqueous dispersion of the top coat comprises an acrylic based polymer or copolymer, and is characterized in that the dry film thereof has a flexibility of at least 570% for a film thickness from about 1.5 to about 2.5 mm, and
wherein the top coat has a viscosity measured on a Brookfield viscometer at 20 rpm with a spindle 3 being from about 40 cP to about 250 cP, and has a solids content from about 25 wt % to about 37 wt %.
10. The foldable paper-based substrate of claim 1 , wherein the paper-based substrate is a recycled or virgin liner, medium, fine paper, newspaper, chipboard, kraftpak paper, paperboard, molded pulp, or any other cellulosic fiber-based substrate, and the foldable paper-based substrate has a basis weight from about 40 g/m 2 to about 1000 g/m 2 .
11. The foldable paper-based substrate of claim 1 , wherein the aqueous dispersion of the primer coat comprises a styrene-butadiene copolymer and is characterized in that the dry film thereof has a flexibility of at least 1350% for a film thickness from about 1.5 to about 2 mm.
12. The foldable paper-based substrate of claim 1 , wherein the aqueous dispersion of the top coat comprises an acrylic based polymer or copolymer, a styrene-butadiene copolymer, a styrene-acrylate copolymer, a styrene-acrylonitrile copolymer or a styrene-acrylonitrile-acrylate copolymer.
13. The foldable paper-based substrate of claim 1 , wherein the top coat is wax free.
14. The foldable paper-based substrate of claim 1 , wherein the primer coat has a viscosity from about 4500 cP to about 5000 cP measured on a Brookfield viscometer at 20 rpm with a spindle 3 .
15. The foldable paper-based substrate of claim 1 , wherein the primer coat further comprises a thickening agent.
16. The foldable paper-based substrate of claim 1 , wherein the top coat has a viscosity from about 40 cP to about 250 cP, the viscosity being measured on a Brookfield viscometer at 20 rpm with a spindle 3 .
17. The foldable paper-based substrate of claim 1 , wherein the top layer has a thickness of about 0.5 μm to about 10 μm.
18. The foldable paper-based substrate of claim 1 , wherein a ratio between a flexibility of a dry film of the primer coat aqueous dispersion and a flexibility of a dry film of the top coat aqueous dispersion is greater than 1 and less than 3.
19. The foldable paper-based substrate of claim 1 , wherein the aqueous dispersion of the primer coat comprises a copolymer of n-butylacrylate, styrene and acrylonitrile, and is characterized in that the dry film thereof has a flexibility of at least 1500% for a film thickness from about 1.6 to about 1.7 mm, and
wherein the primer coat has a viscosity measured on a Brookfield viscometer at 20 rpm with a spindle 3 being from about 4500 cP to about 10000 cP and has a solids content from about 45 wt % to about 55 wt %.
20. The foldable paper-based substrate of claim 1 , wherein the aqueous dispersion of the primer coat comprises a copolymer of n-butylacrylate, styrene and acrylonitrile, and is characterized in that the dry film thereof has a flexibility of at least 1500% for a film thickness from about 1.6 to about 1.7 mm, and the aqueous dispersion of the top coat comprises an acrylic based polymer or copolymer, and is characterized in that the dry film thereof has a flexibility of at least 570% for a film thickness from about 1.5 to about 2.5 mm,
wherein the primer coat has a viscosity measured on a Brookfield viscometer at 20 rpm with a spindle 3 being from about 4500 cP to about 5000 cP, and a solids content from about 45 wt % to about 55 wt %, and
wherein the top coat has a viscosity measured on a Brookfield viscometer at 20 rpm with a spindle 3 being from about 40 cP to about 250 cP, and a solids content from about 25 wt % to about 37 wt %.