According to the present invention, there is provide a coated film that is excellent in surface hardness and abrasion resistance and has good adhesion between a polyester film and a hard coat layer. The present invention relates to a coated film comprising a polyester film and a coating layer formed on at least one surface of the polyester film, the coating layer being prepared from a coating solution comprising a (meth)acrylate compound, a reactive silica comprising a (meth)acryloyl group, and an isocyanate-based compound.
1. A coated film comprising:
a polyester film, and
a coating layer which is formed on at least one surface of the polyester film and prepared from a coating solution,
wherein non volatile components of the coating solution consist solely of:
at least one (meth)acrylate compound,
a reactive silica comprising a (meth)acryloyl group, and
at least one blocked isocyanate in which the blocking agent is an active methylene-based compound.
2. The coated film according to claim 1 , wherein a content of the (meth)acrylate compound in the coating solution is 10 to 95% by weight, a content of the reactive silica comprising a (meth)acryloyl group in the coating solution is 1 to 60% by weight, and a content of the isocyanate-based compound is 1 to 60% by weight, all based on a total amount of whole non-volatile components in the coating solution.
3. The coated film according to claim 1 , wherein the blocked isocyanate has an isocyanurate structure.
4. A coated film comprising:
a polyester film, and
a coating layer which is formed on at least one surface of the polyester film and prepared from a coating solution,
wherein non volatile components of the coating solution consist solely of:
at least one (meth)acrylate compound,
a reactive silica comprising a (meth)acryloyl group,
at least one blocked isocyanate in which the blocking agent is an active methylene-based compound, and
at least one acrylic resin.
5. The coated film according to claim 4 , wherein a content of the acrylic resin in the coating solution is 0.01 to 30% by weight based on the total amount of whole non-volatile components in the coating solution.
6. A coated film comprising:
a polyester film, and
a coating layer which is formed on at least one surface of the polyester film and prepared from a coating solution consisting solely of:
at least one solvent;
at least one (meth)acrylate compound;
at least one reactive silica comprising a (meth)acryloyl group; and
at least one blocked isocyanate in which the blocking agent is an active methylene-based compound.