Active material composite powder, lithium battery, and method for manufacturing the same
Provided is an active material composite powder with which resistance can be reduced, and a method for manufacturing the active material composite powder. The active material composite powder includes an active material and lithium niobate attached onto the surface of the active material, and its BET specific surface area S [m 2 /g] is 0.93<S<1.44, and the method for manufacturing an active material composite powder includes a spraying and drying step of spraying a solution including lithium and a peroxo complex of niobium onto the active material and at the same time drying the solution, and a heating treatment step of carrying out a heating treatment after the spraying and drying step, wherein the temperature of the heating treatment is higher than 123° C. and lower than 350° C.
1. A method for manufacturing an active material composite powder comprising:
a spraying and drying step of spraying a solution including hydrogen peroxide, lithium and a peroxo complex of niobium onto an active material and at the same time drying the solution; and
a heating treatment step of carrying out a heating treatment after the spraying and drying step,
wherein the temperature of the heating treatment is higher than 123° C. and no more than 250° C., and
a BET specific surface area S [m 2 /g] of the active material composite powder is more than 0.93 and less than 1.44.
2. A method for manufacturing a lithium battery including a cathode, an anode, and an electrolyte having contact with the cathode and the anode, the method comprising:
a spraying and drying step of spraying a solution including hydrogen peroxide lithium and a peroxo complex of niobium onto an active material and at the same time drying the solution;
a heating treatment step of carrying out a heating treatment at a temperature higher than 123° C. and no more than 250° C., to make an active material composite powder after the spraying and drying; and
an electrode making step of making the cathode or the anode including the active material composite powder,
wherein a BET specific surface area S [m 2 /g] of the active material composite powder is more than 0.93 and less than 1.44.