Adhesive composition, adhesive film prepared from the same and display member including the same

1. An adhesive composition, comprising:

a monomer mixture including 10 wt % to 40 wt % of a hydroxyl group-containing (meth)acrylate and 60 wt % to 90 wt % of a comonomer; and

organic particles,

the organic particles having an average particle diameter of about 10 nm to about 400 nm,

wherein the comonomer includes an alkyl (meth)acrylate monomer having a glass transition temperature of about −150° C. to about 0° C., and

wherein an adhesive film prepared from the adhesive composition has a ratio of storage modulus at 80° C. to storage modulus at −20° C. of the adhesive film ranges from about 1:1 to about 1:10.

2. The adhesive composition as claimed in claim 1 , wherein the organic particles have a core-shell structure in which the core and the shell have respective glass transition temperatures satisfying Equation 1:

Tg ( c )< Tg ( s )  [Equation 1]

where Tg (c) is a glass transition temperature in degrees Celsius of the core and Tg (s) is a glass transition temperature in degrees Celsius of the shell.

3. The adhesive composition as claimed in claim 2 , wherein the core has a glass transition temperature of about −150° C. to about 10° C. and the shell has a glass transition temperature of about 15° C. to about 150° C.

4. The adhesive composition as claimed in claim 1 , wherein the organic particles are present in an amount of about 0.1 parts by weight to about 15 parts by weight based on 100 parts by weight of the monomer mixture.

5. An adhesive film prepared from the adhesive composition as claimed in claim 1 , the adhesive film comprising:

a hydroxyl group-containing (meth)acrylic copolymer that is polymerized from the monomer mixture; and

the organic particles,

the adhesive film having a storage modulus of about 10 kPa to about 1,000 kPa at 80° C.

6. The adhesive film as claimed in claim 5 , wherein the adhesive film has a glass transition temperature of about 0° C. or less.

7. The adhesive film as claimed in claim 5 , wherein a difference in index of refraction between the organic particles and the hydroxyl group-containing (meth)acrylic copolymer is about 0.1 or less.

8. The adhesive film as claimed in claim 5 , wherein the adhesive film has a storage modulus of about 20 kPa to about 500 kPa at −20° C.

9. The adhesive film as claimed in claim 5 , wherein a ratio of storage modulus at 25° C. to storage modulus at −20° C. of the adhesive film ranges from about 1:1 to about 1:4.

10. The adhesive film as claimed in claim 5 , wherein the adhesive film has a T-peel strength of about 400 gf/in to about 4,000 gf/in, as measured at 25° C. with respect to a corona-treated polyethylene terephthalate film.

11. The adhesive film as claimed in claim 5 , wherein the adhesive film has a T-peel strength of about 200 gf/in to about 3,000 gf/in, as measured at 60° C. with respect to a corona-treated polyethylene terephthalate film.

12. The adhesive film as claimed in claim 5 , wherein the adhesive film has a thickness of about 100 μm and a haze of about 5% or less.

13. The adhesive film as claimed in claim 5 , wherein the adhesive film has a thickness of about 100 μm and a haze of about 5% or less, as measured after the adhesive film is subjected to 200% stretching.

14. The adhesive film as claimed in claim 5 , wherein the adhesive film has a recovery rate of about 30% to about 98%, as represented by Equation 2:

Recovery rate (%)(1−( X f /X 0 ))×100,  [Equation 2]

wherein:

X 0 is an initial thickness of the adhesive film, and

X f is measured as follows:

bonding ends of two polyethylene terephthalate films, each having a thickness of about 75 μm, a length of about 50 mm, and a width of about 20 mm, to each other via the adhesive film having a length of 20 mm and a width of 20 mm by bonding a first end of a first polyethylene terephthalate film to a first end of the adhesive film and then bonding a second end of the adhesive film to a first end of a second polyethylene terephthalate film;

securing first and second jigs to non-bonded ends of the polyethylene terephthalate films;

keeping fixed the first jig and pulling the second jig such that the adhesive film is pulled to a length of 10 times the initial thickness of the adhesive film at a pulling rate of about 300 mm/min and then maintained for 10 seconds;

applying a force of 0 kPa to the adhesive film by recovering the adhesive film at a same rate as the pulling rate; and

measuring an increased length of the adhesive film.

15. The adhesive film as claimed in claim 5 , wherein the adhesive film has a bubble generation area of about 0%, and the bubble generation area is measured by:

bending the adhesive film having a length of 13 cm, a width of 3 cm, and a thickness of 100 μm, and including a 50 μm thick polyethylene terephthalate film stacked on a first surface thereof and a 100 μm thick polyethylene terephthalate film stacked on a second surface thereof towards the 50 μm thick polyethylene terephthalate film such that the adhesive film has half the length,

placing the adhesive film between parallel frames having a gap of about 1 cm, and

aging under conditions of 70° C. and 93% relative humidity for 24 hours.

16. The adhesive film as claimed in claim 5 , wherein the adhesive film does not suffer from detachment or bubble generation after about 100,000 cycles or more, as measured by:

attaching the adhesive film having a thickness of about 100 μm between two corona-treated about 50 μm thick polyethylene terephthalate substrates, and

repeatedly bending at room temperature at a rate of 30 cycles/min such that a radius of curvature of the adhesive film becomes 3 mm, 1 cycle being bending the adhesive film in half once and unfolding the adhesive film back.

17. A display member, comprising:

an optical film; and

an adhesive layer formed of the adhesive composition as claimed in claim 1 ,

wherein the adhesive layer is formed on one or both surfaces of the optical film.

18. The display member as claimed in claim 17 , wherein the optical film includes a touch panel, a window, a polarizing plate, a color filter, a retardation film, an elliptical polarizing film, a reflective film, an anti-reflective film, a compensation film, a brightness improving film, an alignment film, an optical diffusion film, a glass shatter-proof film, a surface protective film, an organic light-emitting diode device barrier layer, a plastic liquid-crystal display substrate, indium tin oxide (ITO) containing films, fluorinated tin oxide (FTO) containing films, aluminum-doped zinc oxide (AZO) containing films, a carbon nanotube-containing film, a Ag nanowire-containing film, or graphene containing film.

19. A display member, comprising:

an optical film; and

the adhesive film as claimed in claim 5 ,

wherein the adhesive film is formed on one or both surfaces of the optical film.

20. The display member as claimed in claim 19 , wherein the optical film includes a touch panel, a window, a polarizing plate, a color filter, a retardation film, an elliptical polarizing film, a reflective film, an anti-reflective film, a compensation film, a brightness improving film, an alignment film, an optical diffusion film, a glass shatter-proof film, a surface protective film, an organic light-emitting diode device barrier layer, a plastic liquid-crystal display substrate, indium tin oxide (ITO) containing films, fluorinated tin oxide (FTO) containing films, aluminum-doped zinc oxide (AZO) containing films, a carbon nanotube-containing film, a Ag nanowire-containing film, or graphene containing film.

21. The adhesive composition as claimed in claim 1 , wherein a difference in index of refraction between the organic particles and a copolymer polymerized from the monomer mixture is about 0.1 or less.