View Patent ↗The powder magnetic core of the present invention can exhibit reliable superposition property in which variance rate of inductance value is small even if superposed current is varied, and can reduce the number of cores used in a reactor. The powder magnetic core comprises: soft magnetic powder particles, and gaps between the soft magnetic powder particles, in which the powder magnetic core has a density ratio of 90 to 95%, and when observing a cross section thereof, layered gaps having thicknesses of 1 to 3 μm and widths of 20 to 200 μm are formed inside of the powder magnetic core. It is desirable that the layered gaps be not less than 50% of all the gaps in a cross sectional area ratio.
1. A powder magnetic core comprising:
soft magnetic powder particles, and
layered gaps between the soft magnetic powder particles,
wherein the layered gaps were formed by pores generated in compacting the soft magnetic powder particles, and
the powder magnetic core has a density ratio of 90 to 95%, and when observing a cross section thereof, the layered gaps having thicknesses of 1 to 3 μm and widths of 20 to 200 μm.
2. The powder magnetic core according to claim 1 , wherein the layered gaps are not less than 50% of all the gaps in a cross sectional area ratio.
3. The powder magnetic core according to claim 1 , wherein the powder magnetic core is constructed by insulator-coated iron based soft magnetic powder in which an insulating layer containing powder metallic oxide and calcium phosphate is formed on the iron based soft magnetic powder and the insulating layer is coated by silicone resin.
4. The powder magnetic core according to claim 1 , wherein decreasing rate of inductance is not more than 30% when superposing from 0 A to 20 A under 20 kHz and 1 V.
5. A reactor comprising the powder magnetic core according to claim 1 .
6. A reactor comprising the powder magnetic core according to claim 2 .
7. A reactor comprising the powder magnetic core according to claim 3 .
8. A reactor comprising the powder magnetic core according to claim 4 .