Self-adhesive material for wood board and wood board
A self-adhesive material for a wood board is described. The self-adhesive material is formed of polyolefin film having a melt index is ≤4 g/10 min (measured at 190° C. and 2.16 kg), and the polyolefin film contains reactive groups with —OH groups of the wood for forming self-adhesive properties. Further, a wood board in which the self-adhesive material is used as a coating and/or as a glue-line material is described.
1. A wood board, in which the wood board comprises wood-based veneers and the wood board is formed so that the veneers of the wood board are joined together, wherein
the wood based veneers are bound together by a self-adhesive material formed of polyolefin film consisting of maleated polyolefin, and
the maleated polyolefin contains maleic anhydride groups as reactive groups which react with —OH groups of the wood for forming covalent bonds between the polyolefin film and —OH groups of the wood-based veneers and the reactive groups of the polyolefin film have been activated at temperatures of more than 180° C. during the manufacturing of the polyolefin film, so that maleic acid has been converted to maleic anhydride and the polyolefin film contains maleic anhydride reactive groups, and
the self-adhesive material is arranged as a glue-line material between the veneers for gluing the veneers together, and
the polyolefin film is bonded directly to a wood surface without any priming and joining layers.
2. The wood board according to claim 1 , wherein the polyolefin film comprises at least two layers which are a first layer and a second layer, and the first layer and the second layer contain the maleic anhydride groups which react with the —OH groups of the veneers.
3. The wood board according to claim 1 , wherein the polyolefin film comprises at least three layers, and the outer layers contain the maleic anhydride groups which react with the —OH groups of the veneers.
4. The wood board according to claim 1 , wherein the polyolefin film has a melt index of less than or equal to 4 g/10 min wherein the melt index is measured at 190° C. and 2.16 kg.
5. The wood board according to claim 1 , wherein the polyolefin film is at least partially cross-linked.
6. The wood board according to claim 1 , wherein the maleic anhydride groups of the polyolefin film are activated at a temperature of more than 180° C. for about 0.5-3 minutes during the manufacturing of the polyolefin film.
7. The wood board according to claim 1 , wherein the maleic anhydride groups of the polyolefin film are activated at a temperature of more than 180° C. for at least 2 minutes by converting the maleic acid to maleic anhydride during the manufacturing of the polyolefin film.
8. The wood board according to claim 1 , wherein the polyolefin film is formed by extrusion.
9. The wood board according to claim 8 , wherein the maleic anhydride groups of the polyolefin film are activated during the extrusion by providing the polyolefin film in a melt for about 2-3 minutes during the extrusion.
10. The wood board according to claim 1 , wherein the maleated polyolefin contains maleic acid in the amount of 0.3-15% by weight of the maleated polyolefin and maleic anhydride.
11. The wood board according to claim 1 , wherein the self-adhesive material is heated and arranged between the veneers of the wood board by hot pressing at temperatures of 120-170° C. for joining the veneers together.
12. The wood board according to claim 1 , wherein the wood board is selected from group consisting of plywood, particle board, fiber board, and paper board.
13. The wood board according to claim 1 , wherein a catalyst is used in the manufacturing of the self-adhesive material.
14. A method for manufacturing a wood board, in which wood-based veneers are joined together to form the wood board, wherein
the wood based veneers are bound together by a self-adhesive material formed of polyolefin film consisting of maleated polyolefin, and
the maleated polyolefin contains maleic anhydride groups as reactive groups which react with —OH groups of the wood for forming covalent bonds between the polyolefin film and —OH groups of the wood-based veneers and the reactive groups of the polyolefin film have been activated at temperatures of more than 180° C. during the manufacturing of the polyolefin film, so that maleic acid has been converted to maleic anhydride and the polyolefin film contains maleic anhydride reactive groups, and
the self-adhesive material is arranged as a glue-line material between the veneers for gluing the veneers together, and
the polyolefin film is bonded directly to a wood surface without any priming and joining layers.