Lithium ion secondary battery
A lithium ion secondary battery includes: a negative electrode having a carbon-based negative electrode material containing graphite particles and amorphous carbon particles; and a positive electrode including a lithium composite oxide. The lithium composite oxide is represented by a general formula: Li x Ni y Mn z Co (1-y-z) O 2 , where x is a numeral of 1 or more and 1.2 or less, and y and z are positive numerals satisfying the relation of y+z<1. The lithium composite oxide has a layer crystal structure and has a median particle diameter (D50) of 4.0 μm or more and less than 6.0 μm.
1. A lithium ion secondary battery comprising:
a negative electrode including a carbon-based negative electrode material containing graphite particles and amorphous carbon particles; and
a positive electrode including a mixture of a first lithium composite oxide and a second lithium composite oxide, wherein:
the first and the second lithium composite oxides are represented by a general formula: Li x Ni y Mn z Co (1-y-z) O 2 , where x is a numeral of 1 or more and 1.2 or less, and y and z are positive numerals satisfying the relation of y+z<1; and
the mixture of the lithium composite oxides has a layer crystal structure comprising:
a median particle diameter (D50) of 4.0 pm or more and does not exceed 5.5 pm,
and
a specific surface area of 0.6 m 2 /g or more and 1.1 m 2 /g or less, and
wherein a ratio y/z in the general formula representing the mixture of the lithium composite oxides is 1.70 or less.
2. The lithium ion secondary battery according to claim 1 , wherein a ratio of a total surface area of the mixture of the lithium composite oxides to a battery capacity is 4.7 to 8.8 m 2 /Ah.
3. The lithium ion secondary battery according to claim 1 , wherein the-first lithium composite oxide is represented by a general formula Li x Ni 1/3 Mn 1/3 Co 1/3 O 2 and the second lithium composite oxide is represented by a general formula Li x Ni 0.4 Mn 0.3 Co 0.3 O 2 .
4. The lithium ion secondary battery according to claim 1 , wherein a weight proportion of the graphite particles included in the negative electrode is 50% or more based on the weight of the carbon-based negative electrode material.
5. The lithium ion secondary battery according to claim 1 , wherein a surface of the mixture of the lithium composite oxides is coated.
6. The lithium ion secondary battery according to claim 1 , wherein the mixture of the lithium composite oxides further includes a doping element.
7. The lithium ion secondary battery according to claim 1 , wherein the mixture of the lithium composite oxides further includes a lithium manganese oxide with a spinel structure.
8. A lithium ion secondary battery comprising:
a negative electrode including a carbon-based negative electrode material containing graphite particles and amorphous carbon particles; and
a positive electrode including a mixture of a first lithium composite oxide and a second lithium composite oxide, wherein:
the first and the second lithium composite oxides are represented by a general formula: Li x Ni y Mn z Co (1-y-z) O 2 , where x is a numeral of 1 or more and 1.2 or less, and y and z are positive numerals satisfying the relation of y+z<1; and
the mixture of the lithium composite oxides has a layer crystal structure comprising:
a median particle diameter (D50) of 4.0 μm or more and does not exceed 5.5 μm, and
a specific surface area of 0.6 m 2 /g or more and 1.1 m 2 /g or less,
wherein a ratio of a total surface area of the mixture of the lithium composite oxides to a battery capacity is 4.7 to 8.8 m 2 /Ah, and
wherein a ratio y/z in the general formula representing the mixture of the lithium composite oxides is 1.70 or less.
9. A lithium ion secondary battery comprising:
a negative electrode including a carbon-based negative electrode material containing graphite particles and amorphous carbon particles; and
a positive electrode including a mixture of a first lithium composite oxide and a second lithium composite oxide,
a separator between the negative electrode and the positive electrode,
wherein:
the first and the second lithium composite oxides are represented by a general formula: Li x Ni y Mn z Co (1-y-z) O 2 , where x is a numeral of 1 or more and 1.2 or less, and y and z are positive numerals satisfying the relation of y+z<1; and
the mixture of the lithium composite oxides has a layer crystal structure comprising:
a median particle diameter (D50) of 4.0 pm or more and does not exceed 5.5 pm, and
a specific surface area of 0.6 m 2 /g or more and 1.1 m 2 /g or less, and
wherein a ratio y/z in the general formula representing the mixture of the lithium composite oxides is 1.70 or less.
10. The method of claim 9 , wherein the separator is a porous film.
11. The method of claim 9 , wherein the separator is a microporous film of polyolefins.
12. The method of claim 9 , wherein a ratio of a total surface area of the mixture of the lithium composite oxides to a battery capacity is 4.7 to 8.8 m2/Ah.