Hot rolled ferritic stainless steel sheet for cold rolling raw material
A heat-resistant cold rolled ferritic stainless steel sheet containing, in mass %, 0.02% or less of C, 0.1% to 1.0% of Si, greater than 0.6% to 1.5% of Mn, 0.01% to 0.05% of P, 0.0001% to 0.0100% of S, 13.0% to 20.0% of Cr, 0.1% to 3.0% of Mo, 0.005% to 0.20% of Ti, 0.3% to 1.0% of Nb, 0.0002% to 0.0050% of B, 0.005% to 0.50% of Al, 0.02% or less of N, with the balance being Fe and inevitable impurities, in which {111}-oriented grains are present at an area ratio of 20% or greater in a region from a surface layer to t/4 (t is a sheet thickness), {111}-oriented grains are present at an area ratio of 40% or greater in a region from t/4 to t/2, and {011}-oriented grains are present at an area ratio of 15% or less in the entire region in a thickness direction.
1. A hot rolled ferritic stainless steel sheet for a material for cold rolling for manufacturing a heat-resistant cold rolled ferritic stainless steel sheet,
the hot rolled ferritic stainless steel sheet consisting of, in terms of mass %,
0.02% or less of C,
0.1% to 1.0% of Si,
greater than 0.6% to 1.5% of Mn,
0.01% to 0.05% of P,
0.0001% to 0.0100% of S,
13.0% to 20.0% of Cr,
0.1% to 3.0% of Mo,
0.05% to 0.20% of Ti,
0.30% to 1.0% of Nb,
0.0002% to 0.0050% of B,
0.005% to 0.45% of Al,
0.02% or less of N, and
the balance of Fe and inevitable impurities,
wherein a sheet thickness of the hot rolled ferritic stainless steel sheet is represented by t′, and a microstructure of the hot rolled ferritic stainless steel sheet in a region from t′/2 to t′/4 is a non-recrystallized microstructure, and
with regard to a microstructure of the heat-resistant cold rolled ferritic stainless steel sheet, a sheet thickness of the heat-resistant cold rolled ferritic stainless steel sheet is represented by t, wherein {111}-oriented grains are present at an area ratio of 20% or greater in a region from a surface layer to t/4, {111}-oriented grains are present at an area ratio of 40% or greater in a region from t/4 to t/2, and {011}-oriented grains are present at an area ratio of 15% or less in the entire region in a thickness direction.
2. A hot rolled ferritic stainless steel sheet for a material for cold rolling for manufacturing a heat-resistant cold rolled ferritic stainless steel sheet,
the hot rolled ferritic stainless steel sheet consisting of, in terms of mass %,
0.02% or less of C,
0.1% to 1.0% of Si,
greater than 0.6% to 1.5% of Mn,
0.01% to 0.05% of P,
0.0001% to 0.0100% of S,
13.0% to 20.0% of Cr,
0.1% to 3.0% of Mo,
0.05% to 0.20% of Ti,
0.30% to 1.0% of Nb,
0.0002% to 0.0050% of B,
0.005% to 0.45% of Al,
0.02% or less of N,
one or more selected from the group consisting of 0.05% to 0.30% of Zr, 0.05% to 0.50% of Co, 0.4% to 2.0% of Cu, 0.1% to 2.0% of Ni, 0.1% to 3.0% of W, and 0.0002% to 0.0100% of Mg and
the balance of Fe and inevitable impurities,
wherein a sheet thickness of the hot rolled ferritic stainless steel sheet is represented by t′, and a microstructure of the hot rolled ferritic stainless steel sheet in a region from t′/2 to t′/4 is a non-recrystallized microstructure, and
with regard to a microstructure of the heat-resistant cold rolled ferritic stainless steel sheet, a sheet thickness of the heat-resistant cold rolled ferritic stainless steel sheet is represented by t, wherein {111}-oriented grains are present at an area ratio of 20% or greater in a region from a surface layer to t/4, {111}-oriented grains are present at an area ratio of 40% or greater in a region from t/4 to t/2, and {011}-oriented grains are present at an area ratio of 15% or less in the entire region in a thickness direction.