Use of charged cellulose nanocrystals for corrosion inhibition and a corrosion inhibiting composition comprising the same
There is provided the use of cellulose nanocrystals as a corrosion inhibitor for inhibiting corrosion of a metal object made of steel. The use includes using acid to impart ester groups onto the cellulose nanocrystals. The use includes dispersing an effective corrosion inhibiting amount of the cellulose nanocrystals having the ester groups within a composition comprising a carrier essentially consisting of water. The cellulose nanocrystals are provided in an amount equal to or greater than 0.1% by weight of the carrier and equal to or less than 3.0% by weight of the carrier. The use includes applying an effective corrosion inhibiting amount of the composition to the metal object such that the composition is adapted to inhibit corrosion of the metal object by 8% or more.
1. The use of cellulose nanocrystals as a corrosion inhibitor for inhibiting corrosion of a metal object made of steel, the use comprising:
using acid to impart ester groups onto the cellulose nanocrystals;
dispersing an effective corrosion inhibiting amount of said cellulose nanocrystals having said ester groups within a composition comprising a carrier essentially consisting of water, the cellulose nanocrystals being in an amount equal to or greater than 0.1 percent by weight of the carrier and equal to or less than 3.0 percent by weight of the carrier; and
applying an effective corrosion inhibiting amount of said composition to the metal object, the composition being adapted to inhibit corrosion of said metal object by 8% or more.
2. The use as claimed in claim 1 , wherein the cellulose nanocrystals are obtained via acid hydrolysis and wherein the ester groups are negatively charged.
3. The use as claimed in claim 1 wherein the acid is sulfuric acid, each of the cellulose nanocrystals has a surface, the ester groups are imparted onto said surfaces of the cellulose nanocrystals, and the ester groups are negatively charged sulfate ester groups.
4. The use as claimed in claim 1 wherein the acid is phosphoric acid, each of the cellulose nanocrystals has a surface, the ester groups are imparted onto said surfaces of the cellulose nanocrystals, and the ester groups are negatively charged phosphate ester groups.
5. The use as claimed in claim 1 wherein the acid is carboxylic acid, each of the cellulose nanocrystals has a surface, the ester groups are imparted onto said surfaces of the cellulose nanocrystals, and the ester groups are negatively charged carboxylate ester groups.
6. The use as claimed in claim 1 wherein the acid is polycarboxilic acid.
7. The use as claimed in claim 1 , wherein the composition further includes an effective corrosion inhibiting amount of at least one of the following compounds: polycarboxilic acid; fatty acid alkanolamide; ammonium benzoate; ethanolamine; monoethaneamine benzoate; ethanol ammonium benzoate; imidazole; tall oil hydroxyethyl imidazoline; 2-imidazoline-1-ethanol, 2-heptadecyl-; 1H-imidazole-1-ethanol, 2-(8-heptadecen-1-yl)-4,5-dihydro-; ethanol, 2-(2-aminoethoxy)-; sodium alkyl naphthalene sulfonate; benzotriazole; 2-mercaptobenzothiazole; 1,2benzisothiazoline-3-1; 2-benzimidazolone; 4,5,6,7-tetrahydrobenzotrazole; tolylimidazolone; tolyltriazole; and 2(5-ethyl-2-pyridyl)benzimidazole.
8. The use as claimed in claim 1 wherein the cellulose nanocrystals have diameters in the range of about 4 nm to about 60 nm and lengths in the range of about 150 nm to about 350 nm.
9. The use as claimed in claim 1 wherein the cellulose nanocrystals are dispersed in a colloidal suspension within the composition in an amount equal to or greater than 0.1 percent by weight of the carrier and equal to or less than 1.0 percent by weight of the carrier.
10. The use as claimed in claim 1 wherein the composition functions to inhibit corrosion by 8% or more when the metal object is exposed to a temperature in the range of about 5 degrees Celsius to about 150 degrees Celsius.
11. The use as claimed in claim 1 , wherein the metal object is exposed to a corrosion environment comprising salt.
12. The use as claimed in claim 7 , wherein the metal object is exposed to a corrosion environment comprising salt.
13. The use of cellulose nanocrystals as a corrosion inhibitor for inhibiting corrosion of a metal object made of steel, the use comprising:
imparting ester groups onto the cellulose nanocrystals;
dispersing an effective corrosion inhibiting amount of said cellulose nanocrystals having said ester groups within a composition comprising a carrier essentially consisting of water, the cellulose nanocrystals being in an amount equal to or greater than 0.1 percent by weight of the carrier and equal to or less than 3.0 percent by weight of the carrier; and
applying an effective corrosion inhibiting amount of said composition to the metal object, the composition being adapted to inhibit corrosion of said metal object by 8% or more.
14. The use as claimed in claim 13 , wherein the ester groups are negatively charged.
15. The use as claimed in claim 13 , wherein the composition further includes an effective corrosion inhibiting amount of at least one of the following compounds: polycarboxilic acid; fatty acid alkanolamide; ammonium benzoate; ethanolamine; monoethaneamine benzoate; ethanol ammonium benzoate; imidazole; tall oil hydroxyethyl imidazoline; 2-imidazoline-1-ethanol, 2-heptadecyl-; 1H-imidazole-1-ethanol, 2-(8-heptadecen-1-yl)-4,5-dihydro-; ethanol, 2-(2-aminoethoxy)-; sodium alkyl naphthalene sulfonate; benzotriazole; 2-mercaptobenzothiazole; 1,2benzisothiazoline-3-1; 2-benzimidazolone; 4,5,6,7-tetrahydrobenzotrazole; tolylimidazolone; tolyltriazole; and 2(5-ethyl-2-pyridyl)benzimidazole.
16. The use as claimed in claim 13 , wherein the composition functions to inhibit corrosion by 8% or more when the metal object is exposed to temperature and pressure conditions that enable the composition to remain in liquid form.
17. The use as claimed in claim 13 wherein the composition functions to inhibit corrosion by 8% or more when the metal object is exposed to a temperature in the range of about 5 degrees Celsius to about 150 degrees Celsius.
18. The use as claimed in claim 13 , wherein the metal object is exposed to a corrosion environment comprising salt.
19. The use of cellulose nanocrystals as a corrosion inhibitor for inhibiting corrosion of a metal object made of aluminium, the use comprising:
using acid to impart ester groups onto the cellulose nanocrystals;
dispersing an effective corrosion inhibiting amount of said cellulose nanocrystals having said ester groups within a composition comprising a carrier essentially consisting of water, the cellulose nanocrystals being in an amount equal to or greater than 0.2 percent by weight of the carrier and equal to or less than 2.0 percent by weight of the carrier; and
applying an effective corrosion inhibiting amount of said composition to the metal object, the composition being adapted to inhibit corrosion of said metal object by 38% or more.
20. The use as claimed in claim 19 wherein the composition functions to inhibit corrosion by between 38% and 71% when the metal object is exposed to a temperature of 35 degrees Celsius.