Carrier for exhaust gas purification catalyst, and exhaust gas purification catalyst
Provided is a carrier for an exhaust gas purification catalyst containing aluminum borate particles having a peak (pore peak) exhibiting the highest intensity in a void volume diameter range of from 20 nm to 100 nm in a logarithmic differential void volume distribution measured using a mercury intrusion porosimeter, in order to provide a new catalyst support capable of effectively suppressing a decrease in catalytic performance caused by sulfur (S) component contained in the exhaust gas, in the case of supporting Pd as a catalytically active component.
1. A carrier for an exhaust gas purification catalyst, comprising aluminum borate particles having a peak exhibiting the highest intensity in a void volume diameter range of from 20 nm to 100 nm in a logarithmic differential void volume distribution measured using a mercury intrusion porosimeter,
wherein a mass ratio of a content of aluminum to a content of boron in the aluminum borate particles is from 8.9 to 35.
2. The carrier for an exhaust gas purification catalyst according to claim 1 , wherein a void having a void volume diameter of from 20 nm to 70 nm accounts for 50% or more of voids having a void volume diameter of from 10 nm to 1000 nm.
3. The carrier for an exhaust gas purification catalyst according to claim 1 , wherein the aluminum borate particles comprise lanthanum (La).
4. The carrier for an exhaust gas purification catalyst according to claim 1 , wherein the aluminum borate particles have a crystal structure represented by 10Al 2 O 3 .2B 2 O 3 or 9Al 2 O 3 .2B 2 O 3 .
5. An exhaust gas purification catalyst comprising the carrier for an exhaust gas purification catalyst according to claim 1 , and Pd as a catalytically active component.
6. A carrier for an exhaust gas purification catalyst, comprising aluminum borate particles having a peak exhibiting the highest intensity in a void volume diameter range of from 20 nm to 100 nm in a logarithmic differential void volume distribution measured using a mercury intrusion porosimeter,
wherein the aluminum borate particles have a crystal structure represented by 10Al 2 O 3 .2B 2 O 3 or 9Al 2 O 3 .2B 2 O 3 and a crystal structure represented by 2Al 2 O 3 .B 2 O 3 .
7. An exhaust gas purification catalyst comprising the carrier for an exhaust gas purification catalyst according to claim 6 , and Pd as a catalytically active component.
8. A carrier for an exhaust gas purification catalyst, comprising aluminum borate particles having a peak exhibiting the highest intensity in a void volume diameter range of from 20 nm to 100 nm in a logarithmic differential void volume distribution measured using a mercury intrusion porosimeter,
wherein the aluminum borate particles have a crystal structure represented by 10Al 2 O 3 .2B 2 O 3 or 9Al 2 O 3 .2B 2 O 3 and a crystal structure represented by Al 2 O 3 .
9. An exhaust gas purification catalyst comprising the carrier for an exhaust gas purification catalyst according to claim 8 , and Pd as a catalytically active component.