Electrode material including small diameter, carbon nanotubes bridging large diameter carbon nanotubes, redox flow battery electrode, redox flow battery, and method for producing electrode material
A redox flow battery includes: first carbon nanotubes having an average diameter of 100 nm or r core, and second carbon nanotubes having an average diameter of 30 nm or less, in which the second carbon nanotubes are adhered to surfaces of the first carbon nanotubes such that the second carbon nanotubes bridge between the plural first carbon nanotubes. Since the redox flow battery includes an electrode material and an electrode including the electrode material, the electromotive force and the charging capacity are high.
1. An electrode material comprising:
first carbon nanotubes having an average diameter of 100 nm or more; and
second carbon nanotubes having an average diameter of 30 nm or less,
wherein the second carbon nanotubes are adhered to surfaces of the first carbon nanotubes such that the individual second carbon nanotubes bridge between the plural first carbon nanotubes, and
when 100 arbitrary second carbon nanotubes are observed with a transmission electron microscope, 10 or more second carbon nanotubes bridge between the plural first carbon nanotubes.
2. The electrode material according to claim 1 ,
wherein the second carbon nanotubes are entangled with the first carbon nanotubes.
3. The electrode material according to claim 1 ,
wherein the average diameter of the first carbon nanotubes is 100 nm to 1000 nm.
4. The electrode material according to claim 1 ,
wherein the average diameter of the second carbon nanotubes is 1 nm to 30 nm.
5. The electrode material according to claim 1 ,
wherein an amount of the second carbon nanotubes added with respect to 100 parts by mass of the first carbon nanotubes is 1 part by mass to 20 parts by mass.
6. The electrode material according to claim 1 ,
wherein an amount of the second carbon nanotubes added with respect to 100 parts by mass of the first carbon nanotubes is 4 part by mass to 17 parts by mass.
7. The electrode material according to claim 1 ,
wherein fiber lengths of the first carbon nanotubes and the second carbon nanotubes are 1 μm to 100 μm.
8. The electrode material according to claim 1 ,
wherein the electrode material is produced by the method comprising
a step of mixing the first carbon nanotubes having the average diameter of 100 nm or more and the second carbon nanotubes having the average diameter of 30 nm or less with each other in a conductive polymer aqueous solution using a wet jet mill.
9. The electrode material according to claim 1 , further comprising
a water-soluble conductive polymer.
10. The electrode material according to claim 9 ,
wherein the water-soluble conductive polymer is a conductive polymer having a sulfo group.
11. A redox flow battery electrode comprising
the electrode material according to claim 1 .
12. A redox flow battery comprising
the redox flow battery electrode according to claim 11 .
13. A method for producing the electrode material according to claim 1 ,
the method comprising
a step of mixing the first carbon nanotubes having the average diameter of 100 nm or more and the second carbon nanotubes having the average diameter of 30 nm or less with each other in a conductive polymer aqueous solution using a wet jet mill.
14. The method for producing an electrode material according to claim 13 ,
wherein the mixing using the wet jet mill is performed at a pressure of 150 MPa or higher.