US 9,786,391 · App. 15/044,747 · Granted Oct 10, 2017

Inventors: Peter Pappano (Poolesville, MD); Martin van Staden (Annapolis, MD)

Assignee: X-ENERGY, LLC

G21C3/28B29C67/0081G21C1/07G21C21/14B33Y10/00B33Y80/00G21C3/62Y02E30/36

Abstract

Claims (55)

1. A method of manufacturing a nuclear fuel element configured for use in a high-temperature gas cooled reactor core, the method comprising:

forming a graphite base portion of the fuel element;

forming a fuel zone of the fuel element, comprising:

forming a first graphite layer on the graphite base portion by depositing graphite powder on the base portion;

depositing a first layer of particles in a predetermined pattern on the first graphite layer by controlling positioning of each particle within the first layer of particles;

forming a second graphite layer on the first layer of particles by depositing graphite powder on the first layer of particles; and

depositing a second layer of particles in a predetermined pattern on the second graphite layer by controlling positioning of each particle within the second layer of particles; and

forming a graphite cap portion of the fuel element,

wherein the particles in the first layer of particles and the second layer of particles comprise nuclear fuel particles.

2. The method of claim 1 , wherein the particles in the first layer of particles and the second layer of particles further comprise burnable poison particles, breeder particles, or a combination thereof.

3. The method of claim 1 , wherein:

forming a first graphite layer on the graphite base portion comprises depositing a mixture of graphite powder and graphite spheres; and

forming a second graphite layer on the first layer of particles comprises depositing a mixture of graphite powder and graphite spheres,

wherein the graphite spheres and the particles are similar in size.

4. The method of claim 1 , wherein the particles in the first layer of particles and the second layer of particles comprise tri-structural-isotropic (TRISO) fuel particles that do not have an overcoat.

5. The method of claim 1 ,

wherein controlling positioning of each particle within the first layer of particles comprises positioning particles in the first layer of particles so that particles of the first layer of particles are spaced apart by substantially the same minimum distance, and

wherein controlling positioning of each particle within the second layer of particles comprises positioning particles in the second layer of particles so that adjacent particles of the second layer are spaced apart by substantially the same minimum distance.

6. The method of claim 1 , wherein the second layer of graphite is formed on the first layer of particles so that the particles of the first layer of particles are separated from particles of the second layer of particles by substantially the same minimum distance.

7. The method of claim 1 , wherein at least one of depositing the first layer of particles and depositing the second layer of particles comprises:

loading particles in controlled positions on a vacuum deposition head;

disposing the vacuum deposition head over the base portion or the first graphite layer;

releasing the particles from the vacuum deposition head; and

pressing the particles into the base portion or the first graphite layer.

8. The method of claim 1 , wherein at least one of depositing the first layer of particles and depositing the second layer of particles comprises:

loading particles in controlled positions on an electrostatic deposition head;

disposing the electrostatic deposition head over the first graphite layer or the second graphite layer;

releasing the particles from the electrostatic deposition head; and

pressing the particles into the first graphite layer or the second graphite layer.

9. The method of claim 1 , wherein at least one of forming the base portion and forming the cap portion, comprises:

A) depositing graphite;

B) pressing the graphite;

C) printing a binder on the pressed graphite; and

repeating operations A, B, and C to form at least one of the base portion and the cap portion.

10. The method of claim 9 , wherein operations A, B, and C are repeated until at least one of the base portion and the cap portion has a thickness ranging from 3 mm to 12 mm.

11. The method of claim 9 , wherein operations A, B, and C are repeated until at least one of the first graphite layer and the second graphite layer has a thickness ranging from about 1 mm to about 3 mm.

12. The method of claim 9 , wherein operation C comprises printing the binder in a pattern having the same shape as a thin section of the fuel element.

13. The method of claim 1 , wherein forming a first graphite layer and forming a second graphite layer comprises:

depositing one of graphite, graphite spheres, or a combination of graphite and graphite spheres to form the graphite layer;

pressing the graphite layer; and

printing a binder on the pressed layer.

14. The method of claim 1 , wherein:

forming a first graphite layer on the graphite base portion comprises depositing graphite spheres; and

forming a second graphite layer on the first layer of particles comprises depositing graphite spheres,

wherein the graphite spheres and the particles are similar in size.

15. The method of claim 3 , wherein depositing a mixture of graphite powder and graphite spheres comprises depositing graphite spheres in a central fuel zone portion and depositing graphite powder in a surrounding portion.

16. The method of claim 1 , wherein:

the first layer of particles is disposed in a first plane;

the second layer of particles is disposed in a second plane that is substantially parallel to the first plane; and

the particles of the first layer do not overlap the particles of the second layer in a direction substantially perpendicular to the first and second planes.

17. The method of claim 1 , wherein the fuel element is a spherical fuel pebble suitable for use in a pebble bed high temperature gas cooled reactor.

18. The method of claim 1 , wherein:

the first layer of particles is disposed in a first plane;

the second layer of particles is disposed in a second plane that is substantially parallel to the first plane; and

the first layer of particles is separated from the second layer of particles by the second graphite layer.