Electrode material for lithium-ion rechargeable battery and method for manufacturing same
An electrode material for a lithium-ion rechargeable battery of the present invention is an electrode material for a lithium-ion rechargeable battery formed by coating a surface of an electrode active material represented by General Formula LiFe x Mn 1-x-y M y PO 4 (here, M represents at least one element selected from Mg, Ca, Co, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, and rare earth elements, 0.05≤x≤1.0, 0≤y≤0.14) with a carbonaceous film, in which an angle of repose is in a range of 35° or more and 50° or less.
1. An electrode material for a lithium-ion rechargeable battery, comprising:
agglomerates of LiFePO 4 primary particles, coated with a calcinated carbonaceous film having a thickness of 1 nm to 5 nm, and an angle of repose in a range of 35° to 50°.
2. The electrode material for a lithium-ion rechargeable battery according to claim 1 ,
wherein an average primary particle diameter of the primary particles is in a range of 30 nm or more and 500 nm or less; and wherein when a cumulative volume percentage of a particle size distribution of the agglomerates is 10%, a particle diameter (D10) is in a range of 1 μm or more and 3 μm or less; and, when the cumulative volume percentage of the particle size distribution of the agglomerates is 90%, the particle diameter (D90) is in a range of 6 μm or more and 18 μm or less.
3. The electrode material for a lithium-ion rechargeable battery according to claim 1 ,
wherein a discharge capacity of the LiFePO 4 at an electric current density of 3 CA is 130 mAh/g or more.
4. A method for manufacturing an electrode material for a lithium-ion rechargeable battery according to claim 1 , comprising:
a step of preparing a mixture made up of the electrode active material, an aromatic organic compound as a first carbon source material, and an organic compound which has a weight-average molecular weight of 500 or less and does not include any aromatic groups as a second carbon source material;
a step of obtaining an agglomerate by spraying and drying the mixture; and
a step of calcinating the agglomerate.
5. The electrode material for a lithium-ion rechargeable battery according to claim 1 , wherein the angle of repose ranges from more than 35° to 50° or less.