Polycarbonate compositions having enhanced optical properties, methods of making and articles comprising the polycarbonate compositions
In some embodiments, a method of making a polycarbonate composition comprises: polymerizing by an interfacial polymerization, reactants comprising a starting material comprising a bisphenol-A to form a bisphenol-A polycarbonate, wherein the bisphenol-A has a purity of greater than or equal to 99.65 wt % and a sulfur content of less than or equal to 2 ppm. The polycarbonate composition has a free hydroxyl content of less than or equal to 150 ppm, and wherein a molded article of the polycarbonate composition has transmission level greater than or equal to 90.0% at 2.5 mm thickness as measured by ASTM D1003-00 and a yellow index (YI) less than or equal to 1.5 as measured by ASTM D1925.
1. A method of making a polycarbonate composition comprising:
polymerizing by an interfacial polymerization, reactants comprising a starting material comprising a bisphenol-A to form a bisphenol-A polycarbonate, wherein the bisphenol-A has a purity of greater than or equal to 99.65 wt % and a sulfur content of less than or equal to 2 ppm;
wherein the polycarbonate composition has a free hydroxyl content of less than or equal to 150 ppm, and wherein a molded article of the polycarbonate composition has transmission level greater than or equal to 90.0% at 2.5 mm thickness as measured by ASTM D1003-00 and a yellow index (YI) less than or equal to 1.5 as measured by ASTM D1925, and wherein the molded article comprises an increase in yellow index (YI) of less than 2 during 2,000 hours of heat aging at 130° C.
2. The method as in claim 1 , comprising dissolving a reactant in an aqueous caustic material, adding the resultant mixture to a solvent medium, and contacting the reactants with a carbonate precursor in presence of a catalyst.
3. The method as in claim 1 , further comprising adding an end-capping agent.
4. The method as in claim 3 , wherein the end-capping agent comprises at least one of the following: phenol or a phenol containing one or more substitutions with at least one of the following: aliphatic groups, olefinic groups, aromatic groups, halogens, ester groups, and ether groups.
5. The method as in claim 4 , wherein the end-capping agent comprises at least one of the following: phenol, p-t-butylphenol, and p-cumylphenol.
6. The method as in claim 1 , wherein the method excludes use of a melt polymerization process to make the polycarbonate.
7. The method of claim 1 , wherein the bisphenol-A polycarbonate is a homopolycarbonate derived from bisphenol-A.
8. The method of claim 7 , wherein the bisphenol-A polycarbonate is a linear homopolycarbonate derived from bisphenol-A.
9. The method of claim 1 , further comprising adding a second polycarbonate derived from bisphenol-A polycarbonate, wherein the second polycarbonate is different than the bisphenol-A polycarbonate.