Propylene-based impact copolymers
A propylene-based impact copolymer (ICP) and composition including the ICP, the ICP comprising a polypropylene homopolymer and within the range of from 10 wt % to 45 wt % of propylene copolymer based on the weight of the ICP, wherein the copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 60 wt % propylene-derived units based on the weight of the propylene copolymer, the propylene-based impact copolymer having a Melt Flow Rate (230° C./2.16 kg) within the range of from 10 g/10 mm to 50 g/10 mm and an Elongation at Break of greater than 70%.
1. A thermoplastic polyolefin composition comprising:
a propylene-based impact copolymer (ICP) comprising a polypropylene homopolymer and within a range of from 10 wt % to 45 wt % of propylene copolymer based on the weight of the ICP, wherein the propylene copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 56 wt % propylene-derived units based on the weight of the propylene copolymer, the propylene-based impact copolymer having a melt flow rate (230° C./2.16 kg) within a range of from 10 g/10 min to 50 g/10 min and an elongation at break of greater than 60%; and
an ethylene-based plastomer and/or propylene-based elastomer;
wherein the impact copolymer is reactor grade granules having an average particle size within a range of from 1200 μm to 2800 μm and produced at a rate greater than 30,000 lbs/hr (13,620 kg/hr).
2. The thermoplastic polyolefin composition of claim 1 , wherein the polypropylene homopolymer forms a continuous phase and the propylene copolymer forms rubber domains having an average size within a range of from 0.40 μm to 0.90 82 m.
3. The thermoplastic polyolefin composition of claim 1 , wherein the propylene-based impact copolymer has a gloss)(60° ) within a range of from 40 to 90% (ASTM D523).
4. The thermoplastic polyolefin composition of claim 1 , wherein the propylene-based impact copolymer has a heat deflection temperature is within a range of from 70° C. to 125° C.
5. The thermoplastic polyolefin composition of claim 1 , wherein the propylene-based impact copolymer has a flexural modulus (1% Secant, ASTM D 790A) is within a range of from 120 kpsi to 300 kpsi.
6. The thermoplastic polyolefin composition of claim 1 , wherein the propylene-based impact copolymer has a tensile strength at yield is within a range of from 2500 psi to 5500 psi.
7. The thermoplastic polyolefin composition of claim 1 , wherein the propylene-based impact copolymer has a notched izod impact at 23° C. as measured by ASTM D256A is greater than 4 ft-lb/in (213 J/m).
8. The thermoplastic polyolefin composition of claim 1 , wherein the propylene-based impact copolymer has a notched izod impact at 23° C. as measured by ISO 180/A is greater than 8 kJ/m 2 .
9. The thermoplastic polyolefin composition of claim 1 , wherein the polypropylene homopolymer has a molecular weight distribution (Mw/Mn) within a range of from 3.0 to 9.0; and wherein the propylene copolymer has a Mw/Mn within a range of from 3.0 to 9.0.
10. The thermoplastic polyolefin composition of claim 1 , wherein the propylene copolymer is an ethylene-propylene copolymer.
11. The thermoplastic polyolefin composition of claim 1 , comprising within a range from 10 wt % to 50 wt % of a high-comonomer impact copolymer, and within a range of from 5 wt % to 30 wt % of the ethylene-based plastomer, and within a range of from 20 wt % to 80 wt % of the propylene-based impact copolymer, wherein the weight percentages are based on the total weight of the composition.
12. The thermoplastic polyolefin composition of claim 11 , having a notched izod impact at 23° C. as measured by ISO 180/A of at least 48 kJ/m 2 at 23° C.; and
a notched izod impact of at least 4 kJ/m 2 at −30° C.
13. The thermoplastic polyolefin composition of claim 11 , having an elongation at break (ISO 527) of at least 70%.
14. The thermoplastic polyolefin composition of claim 11 , having a flexural modulus (chord, ISO 178) of at least 200 MPa.
15. The thermoplastic polyolefin composition of claim 11 , further comprising within a range of from 6 wt % to 30 wt % talc by weight of the composition.
16. An exterior automotive component comprising the thermoplastic polyolefin composition of claim 15 .
17. The thermoplastic polyolefin composition of claim 1 , comprising within a range of from 2 wt % to 25 wt % of an ethylene-based plastomer, within a range of from 2 wt % to 25 wt % of a high-comonomer impact copolymer, and within a range of from 70 wt % to 98 wt % of the propylene-based impact copolymer, wherein the weight percentages are based on the total weight of the composition.
18. The thermoplastic polyolefin composition of claim 17 , having a Notched Izod Impact at 23 ° C. as measured by ISO 180/A of at least 48 kJ/m 2 at 23° C.; and
a Notched Izod Impact of at least 4 kJ/m 2 at −30° C.
19. The thermoplastic polyolefin composition of claim 17 , having an elongation at break (ISO 527) of at least 60%.
20. The thermoplastic polyolefin composition of claim 17 , having a, flexural modulus (chord, ISO 178) of at least 500 MPa.
21. The thermoplastic polyolefin composition of claim 17 , further comprising within a range of from 0.5 wt % to 6.0 wt % talc by weight of the composition.
22. An interior automotive component comprising the thermoplastic polyolefin composition of claim 21 .
23. A thermoplastic polyolefin composition comprising:
a propylene-based impact copolymer (ICP) comprising a polypropylene homopolymer and within a range of from 10 wt % to 45 wt % of propylene copolymer based on the weight of the ICP, wherein the propylene copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 56 wt % propylene-derived units based on the weight of the propylene copolymer, the propylene-based impact copolymer having a melt flow rate (230° C./2.16 kg) within a range of from 10 g/10 min to 50 g/10 min and an elongation at break of greater than 60%; and
an ethylene-based plastomer and/or propylene-based elastomer;
wherein the polypropylene homopolymer forms a continuous phase and the propylene copolymer forms rubber domains having an average size within a range of from 0.40 μm to 0.90 μm.
24. The thermoplastic polyolefin composition of claim 23 , wherein the propylene-based impact copolymer has a gloss)(60° within a range of from 40 to 90% (ASTM D523).
25. The thermoplastic polyolefin composition of claim 23 , wherein the propylene-based impact copolymer has a heat deflection temperature is within a range of from 70° C. to 125° C.
26. The thermoplastic polyolefin composition of claim 23 , wherein the propylene-based impact copolymer has a flexural modulus (1% Secant, ASTM D 790A) is within a range of from 120 kpsi to 300 kpsi.
27. The thermoplastic polyolefin composition of claim 23 , wherein the propylene-based impact copolymer has a tensile strength at yield is within a range of from 2500 psi to 5500 psi.
28. The thermoplastic polyolefin composition of claim 23 , wherein the propylene-based impact copolymer has a notched izod impact at 23° C. as measured by ASTM D256A is greater than 4 ft-lb/in (213 J/m).
29. The thermoplastic polyolefin composition of claim 23 , wherein the propylene-based impact copolymer has a notched izod impact at 23° C. as measured by ISO 180/A is greater than 8 kJ/m 2 .
30. The thermoplastic polyolefin composition of claim 23 , wherein the polypropylene homopolymer has a molecular weight distribution (Mw/Mn) within a range of from 3.0 to 9.0; and wherein the propylene copolymer has a Mw/Mn within a range of from 3.0 to 9.0.