Processes and compositions for cleaning mixing devices to improve polymer production

1. A cleaning mixture, comprising:

water;

thermoplastic polymeric resin pellets having a Rockwell R hardness of from 85 to 140 as measured by ASTM D785; and

a surfactant salt comprises at least one of the following: sulfonate salts, C 6 to C 36 carboxylic acid salts, and mixtures thereof;

wherein the cleaning mixture has a pH from 6.0 to 9.0.

2. The cleaning mixture of claim 1 , wherein the surfactant salt is 0.1 wt % to 9 wt % of the cleaning mixture.

3. The cleaning mixture of claim 1 , wherein the thermoplastic polymeric resin pellets are 70 to 99 wt % of the cleaning mixture.

4. The cleaning mixture of claim 1 , wherein the water is present in an amount of 0.9 to 12.0 wt % of the cleaning mixture.

5. The cleaning mixture of claim 1 , wherein the surfactant salt and the water form an aqueous solution with a pH of 6.0 to 7.0.

6. The cleaning mixture of claim 1 , wherein the surfactant salt and the water form an aqueous solution and the aqueous solution has a viscosity of 20 to 1,000 centipoise as measured by ASTM D445 at 23° C.

7. The cleaning mixture of claim 1 , wherein the thermoplastic polymeric resin pellets comprise cylinders with an average length of 2.0 to 6.0 mm and an average diameter of 0.5 to 4.0 mm.

8. The cleaning mixture of claim 7 , wherein the thermoplastic polymeric resin pellets comprise pellets having at least one angular face and wherein the surfaces defining the angular face meet at an angle of 60 to 120 degrees.

9. The cleaning mixture of claim 8 , wherein the thermoplastic polymeric resin pellets have a bulk density of 0.5 to 0.9 g/cc, as measured by ASTM D1895.

10. The cleaning mixture of claim 1 , wherein the thermoplastic polymeric resin pellets have a bulk density of 0.5 to 0.9 g/cc, as measured by ASTM D1895.

11. The cleaning mixture of claim 1 , wherein the thermoplastic polymeric resin pellets comprise pellets having at least one angular face and wherein the surfaces defining the angular face meet at an angle of 60 to 120 degrees.

12. The cleaning mixture of claim 11 , wherein the angle is 80 to 100 degrees.

13. The cleaning mixture of claim 1 , wherein the surfactant salt comprises at least one of the following: alkyl aryl sulfonate salts and alkyl sulfate salts.

14. The cleaning mixture of claim 1 , wherein the cleaning mixture consists of:

70 to 99 wt % of the thermoplastic polymeric resin pellets; and

1 to 30 wt % of an aqueous solution that contains 0.2 to 30 wt % of the surfactant.

15. The cleaning mixture of claim 1 , wherein the surfactant salt and the water form an aqueous solution and wherein the thermoplastic polymeric resin pellets are externally coated with the aqueous solution.

16. A cleaning mixture, comprising:

water;

thermoplastic polymeric resin pellets having a Rockwell R hardness of from 85 to 140 as measured by ASTM D785; and

a surfactant salt comprises at least one of the following: sulfonate salts, C 6 to C 36 carboxylic acid salts, and mixtures thereof;

wherein the cleaning mixture has a pH from 6.0 to 9.0;

wherein the surfactant salt and the water form an aqueous solution and the aqueous solution has a viscosity of 20 to 1,000 centipoise as measured by ASTM D445 at 23° C.; and

wherein the thermoplastic polymeric resin pellets comprise cylinders with an average length of 2.0 to 6.0 mm and an average diameter of 0.5 to 4.0 mm.

17. The cleaning mixture of claim 14 , wherein the cleaning mixture consists of:

70 to 99 wt % of the thermoplastic polymeric resin pellets; and

1 to 30 wt % of an aqueous solution that contains 0.2 to 30 wt % of the surfactant.

18. The cleaning mixture of claim 15 , wherein the surfactant salt comprises a C 6 to C 36 carboxylic acid salt.

19. The cleaning mixture of claim 15 , wherein the surfactant salt and the water form an aqueous solution and wherein the thermoplastic polymeric resin pellets are externally coated with the aqueous solution.