Honeycomb matrix comprising macroporous desiccant, process and use thereof
Macroporous desiccant based honeycomb matrix containing the macroporous desiccant synthesized “in-situ”, the desiccant having a differential water adsorption. Process for the “in-situ” preparation of the macroporous desiccant based honeycomb matrix including the steps of soaking honeycomb substrate impregnated with water glass, in aqueous metal salt(s) solution or acid solution, or combination thereof, until such time that the hydrogel honeycomb matrix is obtained and thermally activating the hydrogel honeycomb matrix to produce macroporous desiccant based honeycomb matrix.
1. A process for in-situ preparation of a macroporous desiccant based honeycomb matrix comprising the steps of:
i. soaking a honeycomb substrate impregnated with water glass, in 4-25% by weight phosphoric acid, at a temperature of 10-80° C. until such time that a hydrogel honeycomb matrix is obtained;
ii. washing the hydrogel honeycomb matrix; and
iii. thermally activating the hydrogel honeycomb matrix at a temperature of 140° C. to produce the macroporous desiccant based honeycomb matrix.
2. The process as claimed in claim 1 , wherein the hydrogel honeycomb matrix comprises at least one substrate selected from the group consisting of an organic substrate and an inorganic substrate.
3. The process as claimed in claim 2 , wherein the at least one substrate comprises fiber or pulp.
4. The process as claimed in claim 1 , wherein the water glass is neutral grade sodium silicate or potassium silicate.
5. The process as claimed in claim 1 , wherein the honeycomb substrate is soaked for about 15 to 120 minutes to obtain the hydrogel honeycomb matrix.