Thin insulation coatings by sol-gel method
Electrically insulating Al 2 O 3 —SiO 2 thin coatings have been deposited on long-length 316 stainless steel (SS) tape using a reel-to-reel continuous sol-gel dip coating process for co-winding insulation into YBCO pancake coils, a high temperature superconductor magnet technology. Coatings with a thickness of ˜2 μm are achieved after just one dip with a tape withdrawal speed of ˜16 mm/s (1 m/min) and a calcination at 700° C. The coatings were measured to have a room-temperature breakdown voltage of about 100 V, corresponding to a dc dielectric strength of about 50 MV/m. Consequently, this process has low cost and high throughput and produces a thin electrical insulation with excellent thermal, dielectric, and mechanical properties. A new technique has been developed in the coating process to mitigate coating buildup near the edges of the tape.
1. A coating for a metallic tape or wire, comprising:
a material having a uniform thickness surrounding the metallic tape or wire,
wherein the material comprises:
one part by weight alkyl silicate binding material;
two parts by weight anhydrous ethyl alcohol; and
3/10 part by weight aluminum oxide powder.
2. The coating of claim 1 , wherein the alkyl silicate binding material contains at least 19 percent by weight silicon dioxide.
3. The coating of claim 1 , wherein the aluminum oxide powder has a particle size of about 0.3 μm.
4. The coating of claim 1 , wherein the coating is a silica polymer formed from a sol-gel solution.
5. The coating of claim 1 , wherein the uniform thickness is between 2 μm and 8 μm.
6. The coating of claim 1 , wherein the coating is disposed on a high temperature superconducting material.