Transparent autophotorechargeable electrochemical device
A transparent photorechargeable electrochemical device is provided. An n-type semiconductor may be used as a positive-electrode active material in the transparent photorechargeable electrochemical device. A method for photorecharging the device is also provided.
1. A method for photorecharging a transparent photorechargeable electrochemical device which is sealed under inert atmosphere the transparent photorechargeable electrochemical device comprising:
a positive electrode having a transparent conductive carrier on which a positive-electrode film is deposited,
said positive-electrode film comprising titanium dioxide by way of positive-electrode active material,
said titanium dioxide being capable of intercalating and deintercalating ions of an alkali metal M 1 ;
a negative electrode comprising an element chosen from said alkali metal M 1 , an alloy of said alkali metal M 1 , and an intermetallic compound of said alkali metal M 1 ; and
a non-aqueous liquid electrolyte comprising a salt of said alkali metal M 1 and an organic solvent,
said positive and negative electrodes respectively having electrode potentials E 1 and E 2 where E 1 >E 2 , E 1 and E 2 being calculated versus the electrode potential of the M 1 + /M 1 0 couple, the titanium dioxide and the negative electrode being directly in contact with the electrolyte,
said method comprising:
exposing said device, to a source of light waves for at least 30 minutes in order to obtain said recharged device.
2. The method according to claim 1 , wherein the device is exposed on the side of the positive electrode to a source of light waves.
3. The method according to claim 1 , wherein the alkali metal M 1 is choosen from lithium, sodium and potassium.
4. The method according to claim 1 , wherein the titanium dioxide has a specific surface area measured by the B.E.T method ranging from 20 m 2 /g to 500 m 2 /g.
5. The method according to claim 1 , wherein the positive electrode film has a porous structure comprising at least mesopores.
6. The method according to claim 1 , wherein the positive electrode film furthermore comprises at least one dye and/or at least one reflector of light.
7. The method according to claim 1 , wherein the transparent conductive carrier is a transparent conductive glass of FTO, of ITO or of ZITO.
8. The method according to claim 1 , wherein the positive electrode film has a thickness ranging from 0.1 to 25 μm.
9. A method for photorecharging a transparent photorechargeable electrochemical device which is sealed under inert atomosphere comprising:
a positive electrode having a transparent conductive carrier on which a positive-electrode film is deposited,
said positive-electrode film comprising titanium dioxide by way of positive-electrode active material,
said titanium dioxide being capable of intercalating and deintercalating ions of an alkali metal M 1 ;
a negative electrode comprising an element chosen from said alkali metal M 1 , an alloy of said alkali metal M 1 , and an intermetallic compound of said alkali metal M 1 ; and
a non-aqueous liquid electrolyte comprising a salt of said alkali metal M 1 and an organic solvent,
said positive and negative electrodes respectively having electrode potentials E 1 and E 2 where E 1 >E 2 , E 1 and E 2 being calculated versus the electrode potential of the M 1 + /M 1 0 couple,the titanium dioxide and the negative electrode being directly in contact with the electrolyte, said method comprising the step of:
i′) exposing said device, to a source of light waves for at least 10 hours;
ii') using the device of step i′) to power an electrical apparatus; and
iii') letting the device of step ii') relax in open circuit in the dark for at least 6 hours, in order to obtain said recharged device.
10. The method according to claim 9 , wherein the device is exposed on the side of the positive electrode to a source of light waves.
11. The method according to claim 9 , wherein the alkali metal M 1 is chosen from lithium, sodium and potassium.
12. The method according to claim 9 , wherein the titanium dioxide has a specific surface area measured by the B.E.T method ranging from 20 m 2 /g to 500 m 2 /g.
13. The method according to claim 9 , wherein the positive electrode film has a porous structure comprising at least mesopores.
14. The method according to claim 9 , wherein the positive electrode film furthermore comprises at least one dye and/or at least one reflector of light.
15. The method according to claim 9 , wherein the transparent conductive carrier is a transparent conductive glass of FTO, of ITO or of ZITO.
16. The method according to claim 9 , wherein the positive electrode film has a thickness ranging from 0.1 to 25 μm.