Method of laser beam localized-coating
A process is disclosed for laser welding sheet metal plates having an anti-corrosion surface layer pre-coat. The plates are arranged one relative to the other in an edge-butting relationship. Using a laser beam having a first beam spot-size, a laser weld joint is formed along the adjacent edges of the sheet metal plates. Subsequent to forming the laser weld joint, a localized anti-corrosion surface layer is formed at least on the laser weld joint. In particular, a laser beam having a second beam spot-size larger than the first beam spot-size is scanned along the laser weld joint. During the scanning, a flow of a powdered anti-corrosion surface layer material is directed toward a portion of the laser weld joint that is being irradiated by the laser beam. The powdered material is melted by the laser beam and forms a layer adhering to the laser weld joint.
1. A process for laser welding together sheet metal plates, the sheet metal plates each having an anti-corrosion surface layer pre-coat, the process comprising:
arranging the sheet metal plates one relative to the other and such that an edge of one of the plates is adjacent to and in contact with an edge of another one of the plates;
using a first laser beam having a first beam spot-size, forming a laser weld joint along the adjacent edges of the sheet metal plates; and
subsequent to forming the laser weld joint, forming a localized anti-corrosion surface layer at least on the laser weld joint, comprising:
scanning a second laser beam having a second beam spot-size in a scanning direction along the laser weld joint, wherein the second beam spot-size larger than the first beam spot-size;
tilting the second laser beam in a tilt direction to produce an elongated beam spot;
during the scanning, providing a flow of a powdered anti-corrosion surface layer material toward a portion of the laser weld joint that is being irradiated by the laser beam,
wherein the powdered anti-corrosion surface layer material is melted by the laser beam and forms a layer adhering to the laser weld joint; and
wherein the tilt direction is parallel to the scanning direction.
2. The process according to claim 1 , wherein the anti-corrosion surface layer material is zinc or an aluminum-silicon alloy (AlSi).
3. The process according to claim 1 , wherein the sheet metal plates comprise a steel substrate, and wherein the second beam spot-size is selected to heat the powdered anti-corrosion surface layer material to a temperature that is below the melting temperature of the steel substrate and above 400° C.
4. The process according to claim 1 , wherein the localized anti-corrosion layer extends beyond the edges of the laser weld joint and overlaps with the anti-corrosion surface layer pre-coat on each of the sheet metal plates.
5. The process according to claim 1 , wherein the laser weld joint extends between a first side of the sheet metal plates and a second side of the sheet metal plates that is opposite the first side, and wherein the localized anti-corrosion surface layer is formed at least on the laser weld joint along each of the first side and the second side.
6. The process according to claim 1 , comprising:
selecting a flow rate of the powdered anti-corrosion surface layer material for forming a localized anti-corrosion surface layer having a predetermined thickness; and
during the scanning, providing the powdered anti-corrosion surface layer material at the selected flow rate.
7. The process according to claim 1 , comprising:
selecting a particle size of the powdered anti-corrosion surface layer material for forming a localized anti-corrosion surface layer having a predetermined thickness; and
during the scanning, providing the powdered anti-corrosion surface layer material having the selected particle size.
8. The process according to claim 1 , wherein the localized anti-corrosion surface layer has a thickness that is sufficient for corrosion protection.
9. The process according to claim 1 , wherein a single laser head is used to generate the laser beam having the first beam spot-size and to generate the laser beam having the second beam spot-size.
10. The process according to claim 1 , wherein a first laser head is used to generate the laser beam having the first beam spot-size and a second laser head is used to generate the laser beam having the second beam spot-size.
11. The process according to claim 1 , comprising subsequent to forming the localized anti-corrosion surface layer, heating the laser welded sheet metal plates to a temperature that is higher than the melting temperature of the anti-corrosion surface layer material, whereby the subsequent heating causes the anti-corrosion surface layer material to melt and redistribute over a larger area.
12. The process according to claim 1 , comprising, prior to forming the laser weld joint, removing the anti-corrosion surface layer pre-coat along the adjacent edges of each of the sheet metal plates.
13. The process according to claim 1 , wherein the sheet metal plates form one of a part of a multi-piece body side for an automobile, a part of a multi-piece part for an automobile and a part of a door ring for an automobile.
14. A process for joining together metallic parts, comprising:
joining together a first metallic part and a second metallic part at a joining region, at least one of the first metallic part and the second metallic part having an anti-corrosion surface layer pre-coat, and wherein the surface layer pre-coat is disrupted within the joining region during the joining; and
forming a localized anti-corrosion surface layer within a target area that is at least one of within the joining region and adjacent to the joining region, comprising:
scanning a laser beam having a predetermined beam spot-size along a scanning direction through the target area;
tilting the laser beam having the second beam spot-size in a tilt direction to produce an elongated beam spot;
during the scanning, providing a flow of a powdered anti-corrosion surface layer material toward a portion of the target area that is being irradiated by the laser beam,
wherein the powdered anti-corrosion surface layer material is melted by the laser beam and forms a layer adhering to surfaces within the joining region; and
wherein the tilt direction is parallel to the scanning direction.
15. The process according to claim 14 , wherein the joining comprises joining using mechanical fasteners.
16. The process according to claim 14 , wherein the anti-corrosion surface layer material is zinc or an aluminum-silicon alloy (AlSi).
17. The process according to claim 14 , wherein the first and second metallic parts each comprise a steel substrate, and wherein the predetermined beam spot-size is selected to heat the powdered anti-corrosion surface layer material to a temperature that is below the melting temperature of the steel substrate and above 400° C.
18. The process according to claim 14 , wherein the target area extends away from the joining region and overlaps with adjacent surface layer pre-coat that is other than disrupted during the joining.
19. The process according to claim 14 , wherein the joining disrupts the surface layer pre-coat along a first side of the sheet metal plates and along a second side of the sheet metal plates that is opposite the first side, and wherein the target zone comprises a first target zone along the first side and a second target zone along the second side.
20. The process according to claim 14 , comprising:
selecting a flow rate of the powdered anti-corrosion surface layer material for forming a localized anti-corrosion surface layer having a predetermined thickness; and
during the scanning, providing the powdered anti-corrosion surface layer material at the selected flow rate.
21. The process according to claim 14 , comprising:
selecting a particle size of the powdered anti-corrosion surface layer material for forming a localized anti-corrosion surface layer having a predetermined thickness; and
during the scanning, providing the powdered anti-corrosion surface layer material having the selected particle size.
22. The process according to claim 14 , comprising subsequent to forming the localized anti-corrosion surface layer, heating the joined together metallic parts to a temperature that is higher than the melting temperature of the anti-corrosion surface layer material, whereby the subsequent heating causes the anti-corrosion surface layer material to melt and redistribute over a larger area.
23. The process according to claim 14 , wherein the joining comprises laser welding.
24. The process according to claim 23 , comprising, prior to laser welding, removing the anti-corrosion surface layer pre-coat along edges of the metallic parts that are to be welded together.
25. The process according to claim 23 , wherein the localized anti-corrosion layer extends beyond the edges of the laser weld joint and overlaps with the anti-corrosion surface layer pre-coat on each of the sheet metal plates.
26. The process according to claim 23 , wherein the laser weld joint extends between a first side of the sheet metal plates and a second side of the sheet metal plates that is opposite the first side, and wherein the localized anti-corrosion surface layer is formed at least on the laser weld joint along each of the first side and the second side.
27. The process according to claim 23 , wherein a single laser head is used to generate the laser beam having the first beam spot-size and to generate the laser beam having the second beam spot-size.
28. The process according to claim 23 , wherein a first laser head is used to generate the laser beam having the first beam spot-size and a second laser head is used to generate the laser beam having the second beam spot-size.
29. The process according to claim 23 , comprising subsequent to forming the localized anti-corrosion surface layer, heating the laser welded sheet metal plates to a temperature that is higher than the melting temperature of the anti-corrosion surface layer material, whereby the subsequent heating causes the anti-corrosion surface layer material to melt and redistribute over a larger area.
30. The process according to claim 23 , comprising, prior to forming the laser weld joint, removing the anti-corrosion surface layer pre-coat along the adjacent edges of each of the sheet metal plates.
31. The process according to claim 23 , wherein the sheet metal plates form one of a part of a multi-piece body side for an automobile, a part of a multi-piece part for an automobile and a part of a door ring for an automobile.