Method for producing a pozzolanic or latent-hydraulic cement clinker substitute
Methods for producing pozzolanic or latent hydraulic cement clinker substitutes may involve calcining clay with a fuel comprising a mineral substance at temperatures in the range from 500 to 1250° C., preferably from 550 to 1150° C., most preferably from 700 to 900° C. A resulting mixture of mineral substance from the fuel and the calcined clay forms a pozzolanic or latent hydraulic cement clinker substitute, in which a fraction of the mineral substance incorporated into the pozzolanic or latent hydraulic cement clinker substitute by the fuel is 1-60% by weight.
1. A method for producing a pozzolanic or latent-hydraulic cement clinker substitute, the method comprising calcining clay at temperatures of between 500 to 1250 degrees Celsius with a fuel comprising a mineral substance, wherein a resulting mixture of the mineral substance from the fuel and the calcined clay forms the pozzolanic or latent-hydraulic cement clinker substitute that includes 1-60% by weight of the mineral substance, wherein the fuel comprising the mineral substance has a ratio of Al 2 O 3 to SiO 2 of 0.13-1.4% by weight and a CaO content of less than 80% by weight.
2. The method of claim 1 wherein the resulting mixture of the mineral substance from the fuel and the calcined clay forms the pozzolanic or latent-hydraulic cement clinker substitute that includes 20-40% by weight of the mineral substance.
3. The method of claim 1 further comprising adjusting properties of the pozzolanic or latent-hydraulic cement clinker substitute via at least one of a particle size distribution of the fuel used for calcining or a composition of the mineral substance contained in the fuel.
4. The method of claim 1 further comprising adjusting a workability of the pozzolanic or latent-hydraulic cement clinker substitute by comminuting the fuel.
5. The method of claim 1 further comprising regulating a chemical composition of the mineral substance resulting from the calcining by using a mixture of fuels having different mineral substance compositions.
6. The method of claim 1 wherein the calcining is performed in a suspension heat exchanger, a rotary kiln, a fluidized bed, or a multitier furnace.
7. The method of claim 1 wherein the fuel is a flyash having a carbon fraction of at least 0.5% by weight.
8. The method of claim 1 further comprising comminuting the clay to particle sizes of less than 10 mm before the calcining.
9. The method of claim 1 further comprising calculating a fraction of the mineral substance supplied to the calcining so as to cause the pozzolanic or latent-hydraulic cement clinker substitute to have a mixing ratio of the calcined clay to the mineral substance of between 0.5:1 to 20:1.
10. The method of claim 1 wherein the fuel has a particle size of between 0.05 to 1 mm.
11. The method of claim 10 wherein the fuel is coal.
12. A method for producing a pozzolanic or latent-hydraulic cement clinker substitute, the method comprising:
calcining clay at temperatures of between 500 to 1250 degrees Celsius with a fuel comprising a mineral substance, wherein a resulting mixture of the mineral substance from the fuel and the calcined clay forms the pozzolanic or latent-hydraulic cement clinker substitute that includes 1-60% by weight of the mineral substance; and
supplying a flyash to the calcining of the clay and the fuel with the mineral substance.
13. The method of claim 12 wherein the fuel is a flyash having a carbon fraction of at least 0.5% by weight.
14. The method of claim 12 further comprising comminuting the clay to particle sizes of less than 10 mm before the calcining.
15. The method of claim 12 further comprising calculating a fraction of the mineral substance supplied to the calcining so as to cause the pozzolanic or latent-hydraulic cement clinker substitute to have a mixing ratio of the calcined clay to the mineral substance of between 0.5:1 to 20:1.
16. The method of claim 12 wherein the fuel is coal.
17. A method for producing a pozzolanic or latent-hydraulic cement clinker substitute, the method comprising calcining clay at temperatures of between 500 to 1250 degrees Celsius with a fuel comprising a mineral substance, wherein a resulting mixture of the mineral substance from the fuel and the calcined clay forms the pozzolanic or latent-hydraulic cement clinker substitute that includes 1-60% by weight of the mineral substance, wherein the fuel used in the calcining is supplemented with a fuel with a flyash having a carbon fraction of at least 0.5% by weight.
18. The method of claim 17 wherein the calcining is performed in a suspension heat exchanger, a rotary kiln, a fluidized bed, or a multitier furnace.
19. The method of claim 17 wherein the fuel is a flyash having a carbon fraction of at least 0.5% by weight.
20. The method of claim 17 further comprising calculating a fraction of the mineral substance supplied to the calcining so as to cause the pozzolanic or latent-hydraulic cement clinker substitute to have a mixing ratio of the calcined clay to the mineral substance of between 0.5:1 to 20:1.