Polyester tire cord with excellent dimensional stability and method for manufacturing the same

1. A manufacturing method of a polyester tire cord having dimensional stability, the method comprising the steps of:

forming a discharged yarn extruded while a polyester containing 85 mol % or more of ethylene terephthalate units is melted and passed through a nozzle;

forming an undrawn yarn by spinning the discharged yarn;

manufacturing a yarn by multistep drawing the undrawn yarn by passing the yarn through a plurality of draft rollers so that a total draw ratio is 1.60 or less, wherein at least one draft roller of the plurality of draft rollers has a temperature between 200° C. and 250° C. and the remaining draft rollers of the plurality of draft rollers have temperatures less than 95° C.;

plying the yarn by cable / ply twisting at 300˜500 twist/meter; and

dipping the plied yarn, in a dipping solution of an epoxy and a pexul, and then drying, drawing, and heat-setting the plied yarn, before dipping the plied yarn in resorcinol-formaldehyde latex (RFL) and again drying and heat-setting the plied yarn.

2. The manufacturing method of claim 1 , wherein the yarn prior to plying has an inherent viscosity of 0.90 to 1.00, an intermediate elongation (@4.5 g/d) of 6.5% or less, a shrinkage of 2.0% or less, and a sum of intermediate elongation and dry heat shrinkage ratio (E-S) of not more than 8.0%.

3. The manufacturing method of claim 1 , wherein following the dipping treatments, an intermediate elongation (@2.25 g/d) of the polyester tire cord after vulcanization for 20 minutes at 170° C. is E 2 , an intermediate elongation (@2.25 g/d) of the polyester tire cord before vulcanization is E 1 , and a difference between E 2 and E 1 is ΔE, comprises:

ΔE divided by E 1 is 0.5 or less.

4. The manufacturing method of claim 1 , wherein E 2 and E 1 are each measured at 25° C., 60° C., 90° C., and 120° C.

5. A polyester tire cord produced according to the manufacturing method of claim 1 .