Rigid thermoplastic foam densification process and composite structures incorporating the densified rigid thermoplastic foam
Styrenic polymer foams having one or two densified major surfaces are produced by applying heat and pressure ( 4 ) to such surfaces to soften the polymer and collapse cells adjacent to said surface to form a densified skin on such surface. The heated surface or surfaces are then cooled under pressure to form a foam having an undensified core ( 7 ) and densified skins ( 5 ) on one or both sides. The partially densified foams are especially useful for forming laminates in which the foam forms a core. Adhesion to external layers ( 30,32 ) is improved due to the presence of the densified layer.
1. A process for densifying a surface of a styrenic polymer foam, comprising:
a) applying heat and pressure to at least one surface of a starting monolithic thermoplastic styrenic polymer foam which has a starting thickness of at least 25 mm and an elastic limit of 3-10% compression to locally heat said surface to a temperature above the glass transition temperature of the styrenic polymer while applying pressure of at least 50 kPa and up to 300 kPa but not greater than the compressive strength at yield of the starting monolithic thermoplastic polymer foam and collapse cells adjacent to said surface to form a densified skin on such surface and produce a multilayer monolithic foam having an undensified core having a thickness of at least 5 mm and a volume density of no greater than 80 kg/m 3 , and at least one densified surface having an area density of at least 0.6 kg/m 2 and a volume density of at least 200 kg/m 3 , and
b) while maintaining pressure on the densified surface or surfaces of the multilayer monolithic foam, cooling the heated and densified surface(s) of the multilayer monolithic foam from a temperature above the glass transition temperature of the styrenic polymer to 50° C. or below, the maintained pressure being at least 1.5 kPa but insufficient to permanently deform the undensified core.
2. The process of claim 1 , wherein the pressure in steps a) and b) is below the compressive strength of the starting polymer foam.
3. The process of claim 2 , wherein in step a) a densified surface having a volume density of at least 400 kg/m 3 is produced.
4. The process of claim 3 , wherein in step a) a densified surface having an area density of at least 0.8 kg/m 2 is produced.
5. The process of claim 3 , wherein two opposing sides of the polymer foam are densified.
6. The process of claim 5 , wherein the two opposing sides of the foam are densified sequentially by performing steps a) and b) on one side of the foam, and then performing steps a) and b) onto an opposing side of the foam.
7. The process of claim 5 , wherein the two opposing sides of the foam are densified simultaneously by performing steps a) and b) on each of said opposing sides of the foam simultaneously.
8. The process of claim 1 wherein in step a) said heat and pressure are applied by contacting the starting monolithic thermoplastic styrenic polymer foam with a heated platen.
9. The process of claim 8 wherein step b) is performed by contacting the multilayer monolithic foam with a cooling platen that is a temperature below the glass transition temperature of the styrenic polymer.
10. The process of claim 1 wherein step b) is performed by contacting the multilayer monolithic foam with a cooling platen that is a temperature below the glass transition temperature of the styrenic polymer.