Ultrathin, graphene-based membranes for water treatment and methods of their formation and use
Methods are generally provided for forming a membrane. In one embodiment, the method includes: dispersing GO nanoparticles in a solvent; depositing the GO nanoparticles on a support to form a GO membrane; and reducing the GO membrane to form a rGO membrane. Also provided is the rGO membrane formed from such methods, along with a plurality of stacked rGO layers. Methods are also provided for separating water from a water/oil emulsion by, for example, passing water through the rGO membrane.
1. A method of forming a membrane, the method comprising:
dispersing single-layered graphene oxide powder in deionized water to form a single-layered graphene oxide dispersion;
sonicating the dispersion;
centrifuging the dispersion to remove large particles and aggregates from the dispersion;
thereafter, filtering the dispersion through a porous support such that a graphene oxide membrane of layered graphene oxide nanoflakes is formed on the support, the graphene oxide membrane having a thickness of about 2 nm to about 5 nm;
thereafter, reducing the graphene oxide membrane to form a reduced graphene oxide membrane wherein reducing the graphene oxide membrane comprises heating the graphene oxide membrane to a reducing temperature of about 200° C. to about 250° C. in a vacuum of about 1 torr to about 5 torr, or comprises heating the graphene oxide membrane to a reducing temperature of about 150° C. to about 240° C. in the presence of hydrogen, or comprises exposure of the graphene oxide membrane to hydrogen plasma; and
thereafter, etching the reduced graphene oxide membrane with electromagnetic radiation having a wavelength of about 400 nm to about 10 nm or with steam to generate pores of a predetermined size in the reduced graphene oxide membrane.
2. The method of claim 1 , wherein the support comprises aluminum oxide.
3. The method of claim 1 , wherein the support comprises an anodic aluminum oxide porous support.
4. The method of claim 1 , wherein the support defines pores having an average size of about 0.3 nm to about 20 nm.
5. The reduced graphene oxide membrane formed from the method of claim 1 .
6. A method of separating water from a water/oil emulsion, the method comprising passing water through the reduced graphene oxide membrane of claim 5 .
7. The method of claim 1 , wherein the porous support is a polymer support.
8. The method of claim 7 , wherein the polymer is a polyamide.
9. The method of claim 7 , wherein the polymer is a cellulose acetate.
10. The method of claim 1 , wherein the predetermined size of the pores of the reduced graphene oxide membrane is from about 0.3 nm to about 20 nm.
11. The method of claim 1 , wherein the predetermined size of the pores of the reduced graphene oxide membrane is from about 0.4 nm to about 10 nm.