Sintering and shaping method
Provided is a three-dimensional shaped article with relatively high strength and relatively high accuracy. A sintering and shaping method includes: a shaping layer forming process of forming a shaping layer ( 5 ) by using a sintering and shaping material in which inorganic particles ( 2 a ) are included; a process of applying a liquid binding agent ( 8 ), in which inorganic particles ( 8 a ) are included, to a desired region of the shaping layer ( 5 ); a process of curing the liquid binding agent ( 8 ), which is applied, to form a shaping cross-sectional layer (shaping portion ( 5 a )); a process of removing a region (non-shaping portion ( 5 b )) of the shaping layer ( 5 ) to which the liquid binding agent ( 8 ) is not applied; and a process of heating the shaping cross-sectional layer that is laminated for a sintering treatment.
1. A sintering and shaping method, comprising:
a shaping layer forming process of forming a shaping layer by using a sintering and shaping material including first inorganic particles and a thermoplastic binder that binds the first inorganic particles to each other;
a process of applying a liquid binding agent, in which second inorganic particles are included, to a desired region of the shaping layer, the second inorganic particles having a lower sintering initiation temperature, at which sintering is initiated, than the first inorganic particles;
a process of curing the liquid binding agent, which is applied, to form a shaping cross-sectional layer;
a process of removing a region of the shaping layer to which the liquid binding agent is not applied; and
a process of heating the shaping cross-sectional layer for a sintering treatment by performing a degreasing process of heating and decomposing the thermoplastic binder and the liquid binding agent, that has been applied and cured, so that a sintering process of heating and fusing the first inorganic particles and the second inorganic particles is initiated during the degreasing process at a temperature lower than the sintering initiation temperature of the first inorganic particles.
2. The sintering and shaping method according to claim 1 ,
wherein the sintering process of heating and fusing the first inorganic particles and the second inorganic particles is performed at a temperature that is lower than a sintering initiation temperature at which the first inorganic particles initiate sintering.
3. The sintering and shaping method according to claim 1 ,
wherein the shaping layer forming process is performed by heating the sintering and shaping material to a temperature that is equal to or higher than a melting point of the thermoplastic binder.
4. The sintering and shaping method according to claim 1 ,
wherein a ratio between the weight of the first inorganic particles which are included in the shaping cross-sectional layer and the weight of the second inorganic particles which are included in the shaping cross-sectional layer is in a range of 400:1 to 3:1.
5. The sintering and shaping method according to claim 1 ,
wherein a ratio between an average particle size of the first inorganic particles and an average particle size of the second inorganic particles is in a range of 50000:1 to 10:1.
6. The sintering and shaping method according to claim 1 ,
wherein the average particle size of the second inorganic particles is 0.001 micrometers to 10 micrometers.
7. The sintering and shaping method according to claim 1 ,
wherein the first inorganic particles and the second inorganic particles are ceramic particles or metal particles.