Phosphorescent phosphor
A phosphorescent phosphor having a high afterglow luminance is provided. The phosphorescent phosphor comprises, as a matrix, a compound represented by MAl 2 O 4 , the metal element represented by M comprising Sr, Mg and Ba, and the phosphorescent phosphor containing, Eu as an activator, and Dy as a co-activator, wherein the content of Eu, in terms of molar ratio, is 0.001≤Eu/(M+Eu+Dy)≤0.05; the content of Dy, in terms of molar ratio, is 0.004≤Dy/(M+Eu+Dy)≤0.06; the content of Mg, in terms of molar ratio, is 0.02≤Mg/(M+Eu+Dy)≤0.1; the content of Ba, in terms of molar ratio, is 0.03≤Ba/(M+Eu+Dy)≤0.15; and the phosphorescent phosphor contains at least one alkali metal element of the group consisting of Li, Na, K and rubidium (Rb). Mg and Ba as well as the alkali metal element(s) contained in the phosphorescent phosphor provide an excellent phosphorescent phosphor having a high afterglow luminance.
1. A phosphorescent phosphor comprising, as a matrix, a compound MAl 2 O 4 , wherein:
M comprises strontium (Sr), magnesium (Mg), and barium (Ba);
the phosphorescent phosphor contains europium (Eu) as an activator, and dysprosium (Dy) as a co-activator;
a content of europium (Eu), in terms of molar ratio, is 0.001≤Eu/(M+Eu+Dy)≤0.05;
a content of dysprosium (Dy), in terms of molar ratio, is 0.004≤Dy/(M+Eu+Dy)≤0.06;
a content of magnesium (Mg) in terms of molar ratio, is 0.02≤Mg/(M+Eu+Dy)≤0.1;
a content of barium (Ba), in terms of molar ratio, is 0.03≤Ba/(M+Eu+Dy)≤0.15;
the phosphorescent phosphor contains sodium (Na); and
a content of sodium (Na) is 0.06 to 3.2 mmol per mol of a total amount of M, europium (Eu), and dysprosium (Dy).
2. The phosphorescent phosphor according to claim 1 , containing boron (B) in an amount of 0.0004 to 0.024 mol per mol of a total amount of M, europium (Eu), and dysprosium (Dy).
3. The phosphorescent phosphor according to claim 1 , wherein the phosphorescent phosphor is prepared from raw materials including:
a strontium (Sr) raw material;
a magnesium (Mg) raw material;
a barium (Ba) raw material;
an aluminum (Al) raw material;
a europium (Eu) raw material;
a dysprosium of (Dy) raw material;
a sodium (Na) raw material; and
a flux.
4. The phosphorescent phosphor according to claim 3 , wherein the phosphorescent phosphor is prepared by:
mixing the raw materials to form a mixed powder; and
firing the mixed powder in a reducing atmosphere.
5. The phosphorescent phosphor according to claim 1 , wherein the phosphorescent phosphor is prepared from raw materials including:
strontium carbonate (SrCO 3 );
at least one of magnesium oxide (MgO) and basic magnesium carbonate;
barium carbonate (BaCO 3 );
alumina (Al 2 O 3 );
europium oxide (Eu 2 O 3 );
dysprosium oxide (Dy 2 O 3 );
at least one of sodium carbonate (Na 2 CO 3 ); and
boric acid (H 3 BO 3 ) as a flux.
6. The phosphorescent phosphor according to claim 5 , wherein the phosphorescent phosphor is prepared by:
milling the raw materials to form a mixed powder; and
firing the mixed powder at a temperature of 1,200° C. to 1800° C. for a period of 2 to 18 hours in a reducing atmosphere.
7. The phosphorescent phosphor according to claim 1 , wherein the content of sodium (Na) is 0.10 to 3.2 mmol per mol of the total amount of M, europium (Eu), and dysprosium (Dy).
8. The phosphorescent phosphor according to claim 1 , wherein the content of sodium (Na) is 0.06 to 0.61 mmol per mol of the total amount of M, europium (Eu), and dysprosium (Dy).