Non-aqueous electrolyte secondary battery

1. A non-aqueous electrolyte secondary battery comprising a positive electrode having a positive electrode active material layer, a negative electrode having a negative electrode active material layer, and an electrolyte layer having an electrolyte solution containing a non-aqueous solvent,

wherein at least one of the positive electrode active material layer and the negative electrode active material layer comprises:

a core-shell-type electrode material having a particle form in which a core part including an electrode active material is coated with a shell part including a coating agent having a conductive material and a gel-forming polymer in a gel state and having a liquid absorption rate with respect to absorption of the electrolyte solution of 25 to 200%, wherein the liquid absorption rate of the gel-forming polymer with respect to the electrolyte solution is determined with the following equation:

Liquid absorption rate (%)=[(Weight of gel-forming polymer after immersing in electrolyte solution−Weight of gel-forming polymer before immersing in electrolyte solution)/Weight of gel-forming polymer before immersing in electrolyte solution]×100; and

a binder containing styrene-butadiene rubber and carboxymethyl cellulose wherein the binder is dispersed in at least one of the positive electrode active material layer or the negative electrode active material layer.

2. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the conductive material is a carbon material.

3. The non-aqueous electrolyte secondary battery according to claim 1 , wherein a mixing ratio of the gel-forming polymer of the shell part and the conductive material (gel-forming polymer: conductive material) by mass ratio is 8:2 to 2:8.

4. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the gel-forming polymer is a vinyl resin having a vinyl monomer as an essential constituent monomer.

5. The non-aqueous electrolyte secondary battery according to claim 4 , wherein the vinyl resin comprises a vinyl monomer (a1) having a carboxyl group and a vinyl monomer (a2) represented by General Formula (1) below, as vinyl monomers,

[Chemical Formula 1]

CH 2 ═C(R 1 )COOR 2   (1)

wherein R 1 is a hydrogen atom or a methyl group, and R 2 is a branched alkyl group having 4 to 36 carbon atoms.

6. The non-aqueous electrolyte secondary battery according to claim 1 , which is a bipolar type lithium ion secondary battery.

7. The non-aqueous electrolyte secondary battery according to claim 5 , wherein the vinyl resin further comprises a hydroxyalkyl acrylate (a4), as a vinyl monomer.

8. The non-aqueous electrolyte secondary battery according to claim 4 , wherein the vinyl resin is a polymer comprising the vinyl monomer (a1) having a carboxyl group and a nitrogen-containing vinyl compound (a33), as constituent monomers, and

the nitrogen-containing vinyl compound (a33) is an amide group-containing vinyl compound (a33-1); a (meth)acrylate compound (a33-2) selected from the group consisting of dialkyl (1 to 4 carbon atoms) aminoalkyl (1 to 4 carbon atoms) (meth)acrylates and quaternary ammonium group-containing (meth)acrylates; a heterocyclic ring-containing vinyl compound (a33-3); or a nitro group-containing vinyl compound.

9. The non-aqueous electrolyte secondary battery according to claim 8 , wherein the vinyl resin comprises methacrylic acid and N-vinyl-2-pyrrolidone, as constituent monomers.

10. A method for producing the non-aqueous electrolyte secondary battery of claim 1 , wherein the core-shell-type electrode material is obtained by any method of the following (1) to (4):

(1) a method which comprises charging a resin solution containing the gel-forming polymer while stirring, in the presence of the electrode active material, adding the conductive material thereto, and removing a solvent therefrom while stirring;

(2) a method which comprises dissolving the gel-forming polymer in a good solvent thereof, dispersing a powder of the electrode active material in the solution, and adding a poor solvent of the gel-forming polymer to the solution;

(3) a method which comprises dissolving the gel-forming polymer in a good solvent thereof, and spraying the obtained solution on the surface of the electrode active material; and

(4) a method which comprises dissolving the electrode active material, the conductive material and the gel-forming polymer in a good solvent of the gel-forming polymer, and pulverizing a solid content obtained by drying the solution.