Belite sulfoaluminate binder
A hydraulic binder includes a belite sulfoaluminate clinker and silica having a BET specific surface area in nitrogen of at least 50 m 2 /g, the quantity of silica being lower than or equal to 5%, the percentage being expressed as a mass percentage in relation to the mass of the binder.
1. A hydraulic binder comprising a belitic sulfoaluminous clinker and silica having a BET specific surface area under nitrogen of at least 50 m 2 /g, the amount of silica being less than 5%, a percentage expressed by mass based on the binder mass.
2. The hydraulic binder according to claim 1 , wherein the clinker is a belite-calcium-sulfoaluminate-ferrite (BCSAF) clinker.
3. A hydraulic composition comprising water and a hydraulic binder according to claim 1 .
4. A shaped object for the building field comprising a hydraulic binder according to claim 1 .
5. The method for manufacturing a hydraulic binder according to claim 1 , wherein a belitic sulfoaluminous clinker is put into contact with less than 5% of silica, a mass percentage based on the binder mass.
6. The method according to claim 5 , wherein the clinker and the silica are mixed or milled together.
7. A method for improving compressional strength beyond 1 day after mixing of a hydraulic binder comprising a belitic sulfoaluminous clinker, the method comprising mixing less than 5% of silica, a mass percentage based on the binder mass, with a belitic sulfoaluminous clinker, the silica having a BET specific surface area under nitrogen of at least 50 m 2 /g.
8. A hydraulic composition comprising water and a hydraulic binder according to claim 2 .
9. A shaped object for the building field comprising a hydraulic binder according to claim 2 .