Method for manufacturing of slurry for production of battery film

1. A method for manufacturing slurry for coating an anode for use in a lithium battery cell, wherein the method comprises the steps of:

(a) mixing an active material with a binder to obtain a mixture, wherein the active material is selected from a group consisting of Li 4 Ti 5 O 12 , Si(Li 4,4 Si), and Ge(Li 4,4 Ge) and wherein the binder is polyvinylidene fluoride, and

(b) adding an organic carbonate to the mixture to generate the slurry, wherein the step (b) is carried out at temperature above the melting temperature of the organic carbonate, and wherein the slurry does not contain a solvent other than the organic carbonate.

2. The method of claim 1 , wherein the organic carbonate is selected from the group ethylene carbonate, dimethyl carbonate, and diethyl carbonate.

3. A method for manufacturing an anode for a lithium battery cell, wherein the method comprises the steps of:

(a) mixing an active anode material with a binder to obtain a mixture, wherein the active anode material is selected from a group consisting of Li 4 Ti 5 O 12 , Si(Li 4,4 Si), and Ge(Li 4,4 Ge) and wherein the binder is polyvinylidene fluoride;

(b) adding an organic carbonate to the mixture to generate a slurry, wherein the step (b) is carried out at temperature above the melting temperature of the organic carbonate, and wherein the slurry does not contain a solvent other than the organic carbonate;

(c) coating an electrode material with the slurry;

(d) drying the coating on the electrode material by drying the organic carbonate, wherein step (d) comprises a parallel recycling step, wherein the organic carbonate is collected for re-use; and

(e) treating the surface of the slurry so that the anode is prepared for use as an anode in a lithium battery cell.

4. The method of claim 3 , wherein the collected organic carbonate is condensed, filtered and cleaned before re-use.

5. The method of claim 3 , wherein the step (e) comprises one or several of sub-steps of:

(i) rolling the electrode material;

(ii) baking the electrode material; and

(iii) finishing the electrode material for use in the lithium battery cell.

6. The method of claim 3 , wherein the organic carbonate is selected from the group ethylene carbonate, diethyl carbonate, and dimethyl carbonate.

7. A method for manufacturing a lithium ion battery cell, wherein the method comprises the steps of:

(a) manufacturing at least one anode by the method as claimed in claim 3 ,

(b) manufacturing at least one cathode by a method comprising the steps of:

(i) mixing an active cathode material with a cathode binder to obtain a mixture, wherein the active cathode material is selected from a group consisting of LiCoO 2 , LiFePO 4 , LiMn 2 O 4 , LiNiO 2 , Li 2 FePO 4 F, LiCo 1/3 Ni 1/3 O 2 ;

(ii) adding a cathode organic carbonate to the mixture to generate a cathode slurry, wherein step (ii) is carried out at temperature above the melting temperature of the cathode organic carbonate, and wherein the cathode slurry does not contain a solvent other than the cathode organic carbonate;

(iii) coating a cathode material with the cathode slurry;

(iv) drying the coating on the cathode material by drying the cathode organic carbonate, wherein step (iv comprises a parallel recycling step, wherein the cathode organic carbonate is collected for re-use; and

(v) treating the surface of the cathode slurry so that the cathode is prepared for use in a lithium battery cell;

(c) arranging the at least one anode and the at least one cathode in layers with lithium ion permeable membranes in between;

(d) arranging the at least one anode, the at least one cathode, and the permeable membranes in a house with openings; and

(e) filling the house with an electrolyte comprising lithium containing salts and an organic carbonate.

8. The method of claim 7 , wherein step (c) further comprises arranging at least two cathodes and at least two anodes in layers with lithium ion permeable membranes in between and step (d) further comprises arranging the at least two cathodes, the at least two anodes, and the lithium ion permeable membranes in a house with openings.

9. The method of claim 7 , wherein the cathode binder is polyvinylidene fluoride.

10. The method of claim 7 , wherein the cathode organic carbonate is selected from the group ethylene carbonate, diethyl carbonate, and dimethyl carbonate.

11. The method of claim 7 , wherein the organic carbonate used to fill the house is selected from the group ethylene carbonate, diethyl carbonate, and dimethyl carbonate.

12. An anode for a lithium battery cell, wherein the anode is coated with a slurry consisting of active material, binder, and organic carbonate, wherein the active material and binder are mixed to obtain a mixture and organic carbonate is added to the mixture and heated to a temperature above the melting temperature of the organic carbonate;

wherein the active material is selected from a group consisting of Li 4 Ti 5 O 12 , Si(Li 4,4 Si), and Ge(Li 4,4 Ge);

wherein the binder is polyvinylidene fluoride; and

wherein the organic carbonate is selected from the group ethylene carbonate, dimethyl carbonate, and diethyl carbonate.

13. A lithium ion battery cell comprising the anode of claim 12 and a cathode.

14. The lithium ion battery cell of claim 13 , wherein the cathode comprises an active cathode material selected from a group consisting of LiCoO 2 , LiFePO 4 , LiMn 2 O 4 , LiNiO 2 , Li 2 FePO 4 F, LiCo 1/3 Ni 1/3 Mn 1/3 O 2 .