Wax-based fertilizer coatings with polyethylene- or polypropylene-based polymers
Disclosed is a hydrophobic coating material that includes a wax-based material and a polyethylene- or polypropylene-based polymer material. Also disclosed is a coated fertilizer composition that includes a fertilizer granule and the hydrophobic coating material coated on the fertilizer granule. Further disclosed is a method of manufacturing a coated fertilizer composition that includes the steps of providing a fertilizer granule and coating the fertilizer granule with the hydrophobic coating material.
1. A fertilizer coating composition comprising:
a wax-based material comprising a paraffin wax, wherein the paraffin wax comprises the reaction product of an alcohol or an amine with a carboxylic acid or anhydride bearing a hydrocarbon group having about 20 to about 500 carbon atoms; and
a low-density, oxidized polyethylene polymer material, wherein the oxidized polyethylene polymer material comprises about 1% to about 15% by weight of the fertilizer coating composition.
2. The fertilizer coating composition of claim 1 , wherein the oxidized polyethylene polymer material is characterized as having a drop point of about 85° C. to about 140° C., a hardness (determined in accordance with ASTM D-5) of less than about 0.5 dmm to about 6.0 dmm, and a viscosity at 140° C. of about 35 cps to about 400 cps.
3. The fertilizer coating composition of claim 1 , wherein the oxidized polyethylene polymer material comprises about 5% to about 10% by weight of the fertilizer coating composition.
4. A coated fertilizer composition comprising:
a fertilizer granule; and
a hydrophobic coating material coated on the fertilizer granule, wherein the hydrophobic coating material comprises:
a wax-based material; and
a low-density, oxidized polyethylene polymer material, wherein the oxidized polyethylene polymer material comprises about 1% to about 15% by weight of the fertilizer coating composition, wherein the oxidized polyethylene polymer material is characterized as having a drop point of about 85° C. to about 140° C., a hardness (determined in accordance with ASTM D-5) of less than about 0.5 dmm to about 6.0 dmm, and a viscosity at 140° C. of about 35 cps to about 400 cps.
5. The coated fertilizer composition of claim 4 , wherein the oxidized polyethylene polymer material comprises about 5% to about 10% by weight of the fertilizer coating composition.
6. The coated fertilizer composition of claim 4 , wherein the wax-based material comprises a paraffin wax.
7. The coated fertilizer composition of claim 6 , wherein the paraffin wax comprises the reaction product of an alcohol or an amine with a carboxylic acid or anhydride bearing a hydrocarbon group having about 20 to about 500 carbon atoms.
8. A method of manufacturing a coated fertilizer composition comprising the steps of:
providing a fertilizer granule; and
coating the fertilizer granule with a hydrophobic coating material, wherein the hydrophobic coating material comprises:
a wax-based material; and
a low-density, oxidized polyethylene polymer material, wherein the oxidized polyethylene polymer material comprises about 1% to about 15% by weight of the fertilizer coating composition, wherein the oxidized polyethylene polymer material is characterized as having a drop point of about 85° C. to about 140° C., a hardness (determined in accordance with ASTM D-5) of less than about 0.5 dmm to about 6.0 dmm, and a viscosity at 140° C. of about 35 cps to about 400 cps.
9. The method of claim 8 , wherein the oxidized polyethylene polymer material comprises about 5% to about 10% by weight of the fertilizer coating composition.
10. The method of claim 8 , wherein the wax-based material comprises a paraffin wax.
11. The method of claim 10 , wherein the paraffin wax comprises the reaction product of an alcohol or an amine with a carboxylic acid or anhydride bearing a hydrocarbon group having about 20 to about 500 carbon atoms.