Method of manufacturing carbon nanotubes and fibers using catalytic metal oxide nanoparticles
A method for producing carbon nanotubes and/or fibers, such as carbon nanotubes, involves sparging a gas (such as carbon dioxide) through a liquid hydrocarbon (such as crude oil) in the presence of an effective amount of metal oxide particles (such as MgO, Al 2 O 3 , CeO 2 , and/or SiO 2 nanoparticles having a size in the range from about 2 nm to about 10 microns, and which may have a bimodal particle size distribution) at a temperature in a range of between about 70 to about 350° C. to produce carbon nanotubes and fibers having a size range of from about 50 nm to about 20 microns.
1. A method for producing carbon nanotubes, micron-sized carbon tubes, and/or carbon fibers comprising:
sparging a gas through a liquid hydrocarbon in the presence of an effective amount of metal oxide particles at a temperature in a range of between about 70 to about 350° C. to produce carbon nanotubes, micron-sized carbon tubes, and/or carbon fibers, where the metal oxide is selected from the group consisting of magnesium oxide, alumina, cerium oxide, silica, and combinations thereof.
2. The method of claim 1 where the gas is selected from the group consisting of carbon dioxide, argon, and mixtures thereof.
3. The method of claim 1 where the liquid hydrocarbon is crude oil.
4. The method of claim 1 where the effective amount of metal oxide particles concentration ranges from 50 ppm to 10 wt % MgO.
5. The method of claim 1 where the metal oxide particles have a particle size range of from about 2 nanometers to about 10 microns.
6. The method of claim 1 where the metal oxide particles are present in a bimodal particle size distribution where the metal oxide particles have an average particle size between about 90 nm to about 5 microns, where the amount of the metal oxide particles of a size less than 1000 nm is more than the amount of metal oxide particles of a size of 1 micron or greater.
7. The method of claim 1 where the amount of gas sparged through the liquid hydrocarbon based on the liquid hydrocarbon ranges from about 0.1 to about 10 volume %.
8. The method of claim 1 where the sizes of the carbon nanotubes, micron-sized carbon tubes, and/or carbon fibers range from about 50 nm to about 20 microns.
9. The method of claim 1 where the temperature is in the range of about 70 to about 250° C.
10. The method of claim 1 where the metal oxide is selected from the group consisting of alumina, cerium oxide, silica, and combinations thereof.
11. A method for producing carbon nanotubes, micron-sized carbon tubes, and/or carbon fibers comprising:
sparging carbon dioxide gas through a liquid hydrocarbon in the presence of from about 10 to about 500,000 ppm of metal oxide particles, based on the liquid hydrocarbon, at a temperature in a range of between about 70 to about 250° C. to produce carbon nanotubes, micron-sized carbon tubes, and/or carbon fibers, where the metal oxide is selected from the group consisting of magnesium oxide, alumina, cerium oxide, silica, and combinations thereof.
12. The method of claim 11 where the liquid hydrocarbon is crude oil.
13. The method of claim 11 where the metal oxide particles have a particle size range of from about 2 nanometers to about 10 microns.
14. The method of claim 11 where the metal oxide particles are present in a bimodal particle size distribution where the metal oxide particles have an average particle size between about 90 nm to about 5 microns, where the amount of the metal oxide particles of a size less than 1000 nm is more than the amount of metal oxide particles of a size of 1 micron or greater.
15. The method of claim 11 where the amount of gas sparged through the liquid hydrocarbon based on the liquid hydrocarbon ranges from about 0.1 to about 10 volume %.
16. The method of claim 11 where the temperature is in the range of about 70 to about 200° C.
17. The method of claim 11 where the metal oxide is selected from the group consisting of alumina, cerium oxide, and combinations thereof.
18. A method for producing carbon nanotubes, micron-sized carbon tubes, and/or carbon fibers comprising:
sparging carbon dioxide gas through a liquid crude oil in the presence of from about 10 to about 500,000 ppm of metal oxide particles, based on the liquid crude oil, at a temperature in a range of between about 70 to about 350° C. to produce carbon nanotubes, micron-sized carbon tubes, and/or carbon fibers, where the metal oxide particles have a particle size range of from about 2 nanometers to about 10 microns, where the amount of gas sparged through the liquid crude oil based on the liquid crude oil ranges from about 0.1 to about 10 volume %, where the metal oxide is selected from the group consisting of magnesium oxide, alumina, cerium oxide, and combinations thereof.
19. The method of claim 18 where the metal oxide particles are present in a bimodal particle size distribution where the metal oxide particles have an average particle size between about 90 nm to about 5 microns, where the amount of the metal oxide particles of a size less than 1000 nm is more than the amount of metal oxide particles of a size of 1 micron or greater.
20. The method of claim 18 where the amount of nanoparticles present range from about 50 to about 1000 ppm.