Cathode material for low temperature solid oxide fuel cells

1. A method of fabricating a solid oxide fuel cell comprising:

depositing a precursor electrolyte layer on at least a portion of an anode layer;

depositing a precursor cathode layer on at least a surface of the precursor electrolyte layer to form a structure; and

heating the structure to between about 1200° C. and about 1600° C. for between about 5 hours and about 25 hours to form the solid oxide fuel cell comprising the anode layer, an electrolyte layer, and a cathode layer comprised of BaCo 0.4 Fe 0.4 Zr 0.2−x Y x O 3−δ , wherein x is greater than 0 and less than 0.2, and wherein δ is between about 0 and about 0.3.

2. The method of claim 1 , wherein the cathode layer has a thickness of between about 5 microns and about 70 microns.

3. The method of claim 1 , wherein x is between about 0 and about 0.2.

4. The method of claim 1 , wherein the anode layer is comprised of at least one of a BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3−δ —Ni, a BaCe 0.6 Zr 0.3 Y 0.1 O 3−δ —Ni, BaZr 0.8 Y 0.2 O 3−δ —Ni, and a BaCe 0.8 Y 0.2 O 3−δ —Ni and the electrolyte layer is comprised of at least one a BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3−δ- 1.0 wt % NiO, a BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3−δ -1.0 wt % CoO, a BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3−δ -1.0 wt % CuO, a BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3−δ -1.0 wt % ZnO, a BaZr 0.8 Y 0.2 O 3−δ -1.0 wt % NiO, a BaZr 0.8 Y 0.2 O 3−δ -1.4 wt % CuO, a BaZr 0.8 Y 0.2 O 3−δ -1.0 wt % CoO, a BaZr 0.8 Y 0.2 O 3−δ -1.0 wt % ZnO, a BaCe 0.6 Zr 0.3 Y 0.1 O 3−δ -1.3 wt % CuO, a BaCe 0.6 Zr 0.3 Y 0.1 O 3−δ- 1.0 wt % NiO, a BaCe 0.6 Zr 0.3 Y 0.1 O 3−δ -1.0 wt % CoO, a BaCeO 0.6 Zr 0.3 Y 0.1 O 3−δ -1.0 wt % ZnO, a BaCe 0.8 Y 0.2 O 3−δ -1.0 wt % CoO, a BaCe 0.8 Y 0.2 O 3−δ -1.0 wt % NiO, a BaCe 0.8 Y 0.2 O 3−δ -1.0 wt % ZnO, and a BaCe 0.8 Y 0.2 O 3−δ -1.0 wt % CuO.

5. The method of claim 1 , wherein the cathode is a porous film cathode.

6. The method of claim 1 , wherein the anode is comprised of at least one of a BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3−δ —Ni, a BaCe 0.6 Zr 0.3 Y 0.1 O 3−δ —Ni, a BaZr 0.8 Y 0.2 O 3−δ —Ni, and a BaCe 0.8 Y 0.2 O 3−δ —Ni.

7. The method of claim 1 , wherein the cathode further comprises a cathode bone with a formula of BaCe 0.6 Zr 0.3 Y 0.1 O 3−δ .

8. The method of claim 7 , wherein the BaCo 0.4 Fe 0.4 Zr 0.1 Y 0.1 O 3−δ is a plurality of nanoparticles and wherein the plurality of nanoparticles is deposited on at least one wall of the cathode bone.

9. The method of claim 1 , wherein the cathode layer is BaCo 0.4 Fe 0.4 Zr 0.1 Y 0.1 O 3−δ .

10. The method of claim 9 , wherein a thickness of the cathode layer is between about 5 and about 70 microns.

11. The method of claim 1 , wherein x is greater than 0 and less than 0.15.

12. The method of claim 1 , wherein x is 0.1.

13. The method of claim 1 , wherein a gel or paste of the precursor cathode layer comprises a cathode powder and terpinol.

14. The method of claim 13 , wherein the cathode powder comprises BSCF, BCFZ, or BCFZY0.1.

15. The method of claim 1 , further comprising sintering the precursor cathode layer at a temperature between about 700° C. and about 1000° C.

16. The method of claim 15 , wherein the sintering takes between for about 2 hours and about 10 hours.

17. The method of claim 1 , further comprising forming a material for the precursor cathode layer, comprising:

dissolving a cathode material in ammonia hydroxide to form a gel;

heating the gel to a temperature between about 120° C. and about 180° C., for between about 10 hours and about 36 hours to produce a charcoal;

milling the charcoal to form a milled charcoal; and

calcining the milled charcoal at a temperature between about 400° C. and about 800° C. for between about 3 hours and about 10 hours to produce a calcined powder.

18. The method of claim 17 , further comprising:

milling the calcined powder with a solvent for between about 24 hours and about 72 hours to produce a milled powder; and

drying the milled powder at a temperature between about 120° C. and about 250° C., for between about 5 hours and about 10 hours to form the cathode powder.

19. The method of claim 18 , wherein the solvent is at least one of a n-butanol, an isopropanol, an ethanol, an acetone, a methanol, or a toluene.

20. The method of claim 1 , wherein the precursor cathode layer is deposited using a method of at least one of a painting, a dipping, a spraying, a screen printing, a spray coating, a tape casing, or a slot dyeing.