Polarizing plate, method of manufacturing the same, and optical display comprising the same
A polarizing plate, a method of manufacturing the same, and an optical display including the same are provided. A polarizing plate includes a polarizer and a first adhesive layer formed on a lower surface of the polarizer, and the first adhesive layer includes an adhesive resin having a glass transition temperature of about 50° C. or greater, and the first adhesive layer has a haze of about 1% or less at a wavelength of about 380 nm to about 780 nm.
1. A polarizing plate comprising: a polarizer and a first adhesive layer formed on a lower surface of the polarizer,
wherein the first adhesive layer comprises an adhesive resin having a glass transition temperature of about 50° C. or greater, and the first adhesive layer has a haze of about 1% or less at a wavelength of about 380 nm to about 780 nm, and
wherein the first adhesive layer has a tensile modulus of about 10 MPa to less than about 2,000 MPa, as measured in accordance with ASTM D882.
2. The polarizing plate according to claim 1 , wherein the first adhesive layer further comprises a polyisocyanate curing agent modified with an allophanate group.
3. The polarizing plate according to claim 2 , wherein the polyisocyanate curing agent modified with the allophanate group is present in an amount of about 5 parts by weight to about 50 parts by weight based on 100 parts by weight of the adhesive resin.
4. The polarizing plate according to claim 2 , wherein the polyisocyanate curing agent modified with the allophanate group comprises at least one of tetramethylene diisocyanate, hexamethylene diisocyanate, dodecamethylene diisocyanate, and trimethylhexamethylene diisocyanate, modified with the allophanate group.
5. The polarizing plate according to claim 1 , wherein the lower surface of the polarizer is treated by at least one of corona treatment, plasma treatment, and primer treatment.
6. The polarizing plate according to claim 1 , wherein the first adhesive layer is directly formed on the lower surface of the polarizer.
7. The polarizing plate according to claim 1 , wherein the first adhesive layer has a thickness of about 5 μm to about 40 μm.
8. The polarizing plate according to claim 1 , further comprising: a protective layer formed on an upper surface of the polarizer.
9. An optical display comprising the polarizing plate according to claim 1 .
10. A polarizing plate comprising: a polarizer, a first adhesive layer formed on a lower surface of the polarizer, and a second adhesive layer formed on a lower surface of the first adhesive layer,
wherein the first adhesive layer comprises an adhesive resin having a glass transition temperature of about 50° C. or greater, and the first adhesive layer has a haze of about 1% or less at a wavelength of about 380 nm to about 780 nm, and
wherein the polarizing plate has a haze of about 1% or less at a wavelength of about 380 nm to about 780 nm.
11. The polarizing plate according to claim 10 , wherein the second adhesive layer has a lower tensile modulus than the first adhesive layer, as measured in accordance with ASTM D882.
12. The polarizing plate according to claim 11 , wherein the second adhesive layer has a tensile modulus of about 0.01 MPa to less than about 1 MPa, as measured in accordance with ASTM D882.
13. The polarizing plate according to claim 10 , wherein the second adhesive layer has a greater thickness than the first adhesive layer.