Conducting film and method for producing the same
View Patent ↗A conducting film of the present invention includes (A) graphene and/or graphene oxide, and/or derivatives thereof, and (B) a compound having a sulfonic acid group, and/or derivatives thereof, and has a volume resistivity of 1×10 4 Ω·cm or less. A method for producing the conducting film of the present invention includes preparing a dispersion by dispersing a component including (A) graphene and/or graphene oxide, and/or derivatives thereof, and (B) a compound having a sulfonic acid group, and/or derivatives thereof in a dispersion medium, applying the dispersion on a substrate and drying it, and performing heat treatment at a temperature of 100° C. or more. Thereby, the present invention provides a conducting film that has high conductivity and can be applied to a wide range of composites including graphenes, and a method for producing the same.
1. A conducting film comprising:
(A) graphene oxide having an average particle diameter of 2 μm or more, and/or derivatives thereof; and
(B) a compound having an aromatic sulfonic acid group (excluding a polymer having a sulfonic acid group),
wherein the conducting film is subjected to a heat treatment at a temperature of more than 100° C. and 250° C. or less for a heat treatment time of from 10 minutes to 6 hours, and
the conducting film has a volume resistivity of from 1×10 −5 Ω·cm or more and 1×10 4 ·cm or less, and has a thickness in a range from 0.003 mm to 0.5 mm.
2. The conducting film according to claim 1 , wherein the component (B) is at least one material selected from a monomer and an oligomer having a sulfonic acid group.
3. The conducting film according to claim 1 , wherein a composition ratio of the components (A) and (B) is such that a content of the component (B) is 3 parts by mass or more and 200 parts by mass or less with respect to 100 parts by mass of the component (A).
4. The conducting film according to claim 1 , further comprising a polymer excluding a polymer having a sulfonic acid group as a component (C).
5. The conducting film according to claim 4 , wherein the component (C) is a non-conductive polymer.
6. The conducting film according to claim 1 , wherein the component (A) is graphene oxide including a multilayered body produced by oxidation decomposition of graphite.
7. A method for producing the conducting film of claim 1 , comprising:
preparing a dispersion by dispersing a component comprising (A) graphene oxide having an average particle diameter of 2 μm or more, and/or derivatives thereof, and (B) a compound having a sulfonic acid group in a dispersion medium,
applying the dispersion on a substrate and drying it, and performing heat treatment at a temperature of 100° C. or more, thereby obtaining a conducting film having a volume resistivity of 1×10 4 Ω·cm or less and a thickness in a range from 0.003 mm to 0.5 mm.
8. The method for producing a conducting film according to claim 7 , wherein the heat treatment condition comprises a heat treatment temperature of more than 100° C. and 250° C. or less.
9. The method for producing a conducting film according to claim 7 , wherein the heat treatment condition comprises a heat treatment time in a range from 10 minutes to 6 hours.
10. The method for producing a conducting film according to claim 7 , wherein the dispersion medium is water or an organic solvent.
11. The method for producing a conducting film according to claim 7 , wherein the conducting film produced is peeled off and separated from the substrate.