Package wrapping including PLA film with moisture barrier by atomic layer deposition
Provided herein is a moisture barrier film for packaging, such as tobacco or cigarette packaging. The film comprises polylactic acid (“PLA”) that is both biodegradable and transparent. The film includes multiple layers of PLA, with a base layer having a relatively high melting point compared to two outer layers, which have a relatively low melting point. The outer layers provide heat sealing capabilities to the film. The film is coated with a metal oxide layer comprised of aluminum oxide, titanium oxide, and/or aluminum-titanium oxide using an atomic layer deposition (“ALD”) coating method. The ALD coating to the PLA film results in a moisture transmission rate of less than 4 g/m2/day after the film has been subjected to creasing, which induces cracking of the ALD metal oxide layer.
1. A package comprising:
a main body formed of a paper material;
a top formed of the paper material;
a central compartment formed by the top and the main body; and
a wrapping formed of a film comprising:
a base layer comprising a first material having a first melting point;
an outer layer comprising a second material having a second melting point, the second melting point is lower than the first melting point, a first side of the outer layer bonded to a first side of the base layer;
an inner layer comprising the second material, a first side of the inner layer bonded to a second side of the base layer, the second side of the base layer opposite the first side of the base layer; and
a moisture barrier coating applied to each of a second side of the outer layer and a second side of the inner layer opposite the first side of the inner layer, the moisture barrier coating comprising a metal-oxide deposited using atomic layer deposition and having a thickness of 2-10 nm.
2. The package of claim 1 , wherein the first material is a first polylactic acid material, and the second material is a second polylactic acid material.
3. The package of claim 2 , wherein at least one of the first polylactic acid material or the second polylactic acid material are corn-based.
4. The package of claim 1 , wherein the first material is a bio-based polypropylene.
5. The package of claim 1 , wherein the moisture barrier coating is transparent.
6. The package of claim 1 , wherein the moisture barrier coating is at least one of an aluminum oxide, a titanium oxide, or an aluminum-titanium oxide.
7. The package of claim 1 , wherein the film has a moisture transmission rate of less than 4 grams per meter squared per day.
8. The package of claim 7 , wherein the film has a moisture transmission rate of less than 2 grams per meter squared per day.
9. The package of claim 1 , wherein the film is between of 15 to 30 microns in thickness.
10. A film comprising:
a base layer comprising a first material having a first melting point;
an outer layer comprising a second material having a second melting point, the second melting point is lower than the first melting point, a first side of the outer layer bonded to a first side of the base layer;
an inner layer comprising the second material, a first side of the inner layer bonded to a second side of the base layer, the second side of the base layer opposite the first side of the base layer; and
a moisture barrier coating applied to each of a second side of the outer layer and a second side of the inner layer opposite the first side of the inner layer, the moisture barrier coating comprising a metal-oxide deposited using atomic layer deposition and having a thickness in a range of 2-10 nm.
11. The film of claim 10 , wherein the first material is a first polylactic acid material, and the second material is a second polylactic acid material.
12. The film of claim 11 , wherein at least one of the first polylactic acid material or the second polylactic acid material are corn-based.
13. The film of claim 10 , wherein the moisture barrier coating is at least one of an aluminum oxide, a titanium oxide, or an aluminum-titanium oxide.