Method for producing inorganic substance powder highly-oriented thin film sheet
The problem addressed by the invention lies in providing a method for producing an inorganic substance powder highly-oriented thin film sheet with which it is possible to produce a sheet of uniform thickness while preventing the generation of impurities, improving sheet surface properties, adjusting apparent specific gravity, and the like. The method for producing a thin film sheet comprises a step for preparing a predetermined inorganic substance powder, thermoplastic resin, and auxiliary agent, a step for exposing the starting materials mixed at a predetermined mixture ratio to high shear stress while kneading, a step for feeding the kneaded starting materials to a T die-type extrusion molding device and molding a sheet, and a step for adjusting the apparent gravity as desired by stretching under predetermined conditions.
1. A thin film sheet for printing that consists of a thermoplastic resin and inorganic substance powder and at least one optional auxiliary agent selected from the group consisting of a lubricant, a fluidity improving agent, a dispersant, an antioxidant, a UV absorbing agent, and a stabilizer,
wherein the thermoplastic resin is high density polyethylene,
wherein a weight ratio of the thermoplastic resin to the inorganic substance powder is 18:82 to 40:60, the inorganic substance powder has an average particle size of 0.5 to 15 μm and is free of particles with a particle size of at least 50 μm,
wherein the film sheet has an apparent specific gravity of 0.55 to 1.40,
wherein the high density polyethylene has a melt mass flow rate of 0.02 to 1.2 g/10 min, and
wherein the inorganic substance powder is at least one selected from the group consisting of calcium carbonate, clay, silica, titanium oxide, talc, kaolin and aluminum hydroxide.
2. The thin film sheet according to claim 1 , wherein the average particle size of the inorganic substance powder is 4.3 to 15 μm.
3. The thin film sheet of claim 1 , wherein the high density polyethylene has a melt mass flow rate of 0.27 to 0.8 g/10 min.
4. The thin film sheet of claim 1 , wherein 50% by weight to 100% by weight of the high-density polyethylene resin has a melt mass-flow rate of 0.02 to 0.5 g/10 min, and remainder of the high-density polyethylene resin has a melt mass-flow rate of 0.5 to 1.2 g/10 min.