Compounds comprising a hibonite structure and a method for their use
Novel colored compounds with a hibonite structure and a method for making the same are disclosed. The compounds may have a formula AAl 12−x−y M a x M b y O 19 where A is typically an alkali metal, an alkaline earth metal, a rare earth metal, Pb, Bi or any combination thereof, and M a is Ni, Fe, Cu, Cr, V, Mn, or Co or any combination thereof, and M b is Ti, Sn, Ge, Si, Zr, Hf, Ga, In, Zn, Mg, Nb, Ta, Sb, Mo, W or Te or any combination thereof. Compounds with varying colors, such as blue, can be made by varying A, M a and M b and their relative amounts. Compositions comprising the compounds and methods for making and using the same are also disclosed.
1. A compound having a formula AAl 12−x−y M a x M b y O 19 , wherein:
A is selected from Ca, Sr, Ba, Mg, Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Li, Na, K, Rb, Cs, Pb, Bi or any combination thereof;
M a is selected from Ni, Fe, Cu, Cr, V, Mn, or Co or any combination thereof;
M b is selected from Ti, Sn, Ge, Si, Zr, Hf, Ga, In, Zn, Mg, Nb, Ta, Sb, Mo, W or Te or any combination thereof;
x is from 0.01 to less than 12;
y is from 0 to less than 12;
x+y is less than 12; and
if y is 0, then x is from 0.01 to less than 1;
if M a comprises Fe, then y is greater than 0, or M a further comprises Ni, Cu, Cr, V, Mn, or Co or any combination thereof; and
if M a is Mn and M b is Mg, then x+y is less than 1, or x+y is greater than 1.
2. The compound of claim 1 , wherein x is from 0.01 to less than 12 and y is from 0.01 to less than 12.
3. The compound of claim 1 , wherein:
A is A 1 1−z A 2 z ;
A 1 is selected from Ca, Sr, Ba, Mg, Sc, Y, Li, Na, K, Rb, Cs, Pb, Bi or any combination thereof;
A 2 is selected from La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu or any combination thereof; and
z is from 0 to less than 1.
4. The compound of claim 1 , wherein the compound is selected from CaAl 11.8 Ni 0.2 O 19 , CaAl 11.5 Ni 0.5 O 19 , CaAl 11 Sn 0.5 Ni 0.5 O 19 , CaAl 10 SnNiO 19 , CaAl 11 Zn 0.5 Ni 0.5 O 19 , CaAl 11 Ge 0.5 Ni 0.5 O 19 , CaAl 10 GeNiO 19 , CaAl 11 Ga 0.5 Ni 0.5 O 19 , CaAl 11 Ti 0.5 Ni 0.5 O 19 , CaAl 10 Ti 0.5 Si 0.5 NiO 19 , CaAl 10 Ti 0.5 Ge 0.5 NiO 19 , CaAl 10 Ti 0.5 Sn 0.5 NiO 19 , CaAl 8 TiSnNi 2 O 19 , CaAl 10 TiNi 0.5 Cu 0.5 O 19 , CaAl 10 TiNi 0.5 Cr 0.5 O 19 , CaAl 10 TiNi 0.5 Zn 0.5 O 19 , CaAl 11.8 Ti 0.1 Ni 0.1 O 19 , CaAl 11.6 Ti 0.2 Ni 0.2 O 19 , CaAl 11.4 Ti 0.3 Ni 0.3 O 19 , CaAl 11.2 Ti 0.4 Ni 0.4 O 19 , CaAl 11 Ti 0.5 Ni 0.5 O 19 , CaAl 10.8 Ti 0.6 Ni 0.6 O 19 , CaAl 10.6 Ti 0.7 Ni 0.7 O 19 , CaAl 10.4 Ti 0.8 Ni 0.8 O 19 , CaAl 10.2 Ti 0.9 Ni 0.9 O 19 , CaAl 10 TiNiO 19 , CaAl 9.6 Ti 1.2 Ni 1.2 O 19 , CaAl 8 Ti 2 Ni 2 O 19 , Ca 0.8 Sr 0.2 Al 11.6 Ti 0.2 Ni 0.2 O 19 , Ca 0.6 Sr 0.4 Al 11.2 Ti 0.4 Ni 0.4 O 19 , Ca 0.4 Sr 0.6 Al 10.8 Ti 0.6 Ni 0.6 O 19 , Ca 0.2 Sr 0.8 Al 10.4 Ti 0.8 Ni 0.8 O 19 , SrAl 10 TiNiO 19 , SrAl 9.6 Ti 1.2 Ni 1.2 O 19 , SrAl 11 Ti 0.5 Ni 0.5 O 19 , SrAl 8 Ti 2 Ni 2 O 19 , Ca 0.5 Sr 0.5 Al 8 Ti 2 Ni 2 O 19 , Ca 0.5 Sr 0.5 Al 10 TiNiO 19 , Ca 0.5 Sr 0.5 Al 10 GeNiO 19 , Ca 0.5 Sr 0.5 Al 11 Sn 0.5 Ni 0.5 O 19 , Ca 0.5 Sr 0.5 Al 10 SnNiO 19 , Sr 0.9 La 0.1 Al 11.9 Ni 0.1 O 19 , Sr 0.8 La 0.2 Al 11.8 Ni 0.2 O 19 , Sr 0.7 La 0.3 Al 11.7 Ni 0.3 O 19 , Sr 0.6 La 0.4 Al 11.6 Ni 0.4 O 19 , Sr 0.5 La 0.5 Al 11.5 Ni 0.5 O 19 , Sr 0.4 La 0.6 Al 11.4 Ni 0.6 O 19 , Sr 0.3 La 0.7 Al 11.3 Ni 0.7 O 19 , Sr 0.2 La 0.8 Al 11.2 Ni 0.8 O 19 , Sr 0.1 La 0.9 Al 11.1 Ni 0.9 O 19 , Ca 0.9 La 0.1 Al 11.9 Ni 0.1 O 19 , Ca 0.8 La 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.7 La 0.3 Al 11.7 Ni 0.3 O 19 , Ca 0.6 La 0.4 Al 11.6 Ni 0.4 O 19 , Ca 0.5 La 0.5 Al 11.5 Ni 0.5 O 19 , Ca 0.4 La 0.6 Al 11.4 Ni 0.6 O 19 , Ca 0.3 La 0.7 Al 11.3 Ni 0.7 O 19 , Ca 0.2 La 0.8 Al 11.2 Ni 0.8 O 19 , Ca 0.1 La 0.9 Al 11.1 Ni 0.9 O 19 , Ca 0.75 La 0.25 Al 11.25 Ti 0.25 Ni 0.5 O 19 , Ca 0.5 La 0.5 Al 11 Ti 0.25 Ni 0.75 O 19 , Ca 0.5 La 0.5 Al 10.5 Ti 0.5 NiO 19 , Ca 0.25 La 0.75 Al 9.75 Ti 0.75 Ni 1.5 O 19 , Ca 0.5 La 0.5 Al 8.5 Ti 1.5 Ni 2 O 19 , LaAl 9 TiNi 2 O 19 , Ca 0.5 La 0.5 Al 11 In 0.5 Ni 0.5 O 19 , Ca 0.5 La 0.5 Al 11 Ga 0.5 Ni 0.5 O 19 , Ca 0.5 La 0.5 Al 11 Ge 0.25 Ni 0.75 O 19 , Ca 0.5 La 0.5 Al 11 Sn 0.25 Ni 0.75 O 19 , Ca 0.75 La 0.25 Al 11.75 Ni 0.25 O 19 , Ca 0.5 Y 0.5 Al 11 Ti 0.25 Ni 0.75 O 19 , Ca 0.5 Ce 0.5 Al 11 Ti 0.25 Ni 0.75 O 19 , Ca 0.5 Pr 0.5 Al 11 Ti 0.25 Ni 0.75 O 19 , Ca 0.5 Na 0.5 Al 10.5 TiNi 0.5 O 19 , Ca 0.5 K 0.5 Al 10.5 TiNi 0.5 O 19 , Ca 0.5 Rb 0.5 Al 10.5 TiNi 0.5 O 19 , Ca 0.5 Cs 0.5 Al 10.5 TiNi 0.5 O 19 , Ca 0.8 Mg 0.2 Al 11.6 Ti 0.2 Ni 0.2 O 19 , Ca 0.5 Ba 0.5 Al 8 Ti 2 Ni 2 O 19 , Sr 0.9 Y 0.1 Al 11.9 Ni 0.1 O 19 , Sr 0.8 Y 0.2 Al 11.8 Ni 0.2 O 19 , Sr 0.8 Ce 0.2 Al 11.8 Ni 0.2 O 19 , Sr 0.8 Nd 0.2 Al 11.8 Ni 0.2 O 19 , Sr 0.8 Pr 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.9 Y 0.1 Al 11.9 Ni 0.1 O 19 , Ca 0.8 Y 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.7 Y 0.3 Al 11.7 Ni 0.3 O 19 , Ca 0.6 Y 0.4 Al 11.6 Ni 0.4 O 19 , Ca 0.5 La 0.5 Al 10.5 Zn 0.5 Sn 0.5 Ni 0.5 O 19 , Ca 0.5 La 0.5 Al 10.5 Cu 0.5 Sn 0.5 Ni 0.5 O 19 , Ca 0.8 Sc 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.8 Yb 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.7 Sr 0.3 Al 11.5 Ni 0.5 O 19 , CaAl 7 Ti 1.5 Ge 0.5 MgNi 2 O 19 , Ca 0.9 Ce 0.1 Al 11.9 Ni 0.1 O 19 , Ca 0.8 Ce 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.7 Ce 0.3 Al 11.7 Ni 0.3 O 19 , Ca 0.6 Ce 0.4 Al 11.6 Ni 0.4 O 19 , Ca 0.5 Ce 0.5 Al 11.5 Ni 0.5 O 19 , Ca 0.4 Ce 0.6 Al 11.4 Ni 0.6 O 19 , Ca 0.3 Ce 0.7 Al 11.3 Ni 0.7 O 19 , Ca 0.2 Ce 0.8 Al 11.2 Ni 0.8 O 19 , Ca 0.1 Ce 0.9 Al 11.1 Ni 0.9 O 19 , Ca 0.9 Pr 0.1 Al 11.9 Ni 0.1 O 19 , Ca 0.8 Pr 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.7 Pr 0.3 Al 11.7 Ni 0.3 O 19 , Ca 0.6 Pr 0.4 Al 11.6 Ni 0.4 O 19 , Ca 0.5 Pr 0.5 Al 11.5 Ni 0.5 O 19 , Ca 0.4 Pr 0.6 Al 11.4 Ni 0.6 O 19 , Ca 0.3 Pr 0.7 Al 11.3 Ni 0.7 O 19 , Ca 0.2 Pr 0.8 Al 11.2 Ni 0.8 O 19 , Ca 0.1 Pr 0.9 Al 11.1 Ni 0.9 O 19 , Ca 0.9 Nd 0.1 Al 11.9 Ni 0.1 O 19 , Ca 0.8 Nd 0.2 Al 11.8 Ni 0.2 O 19 , Ca 0.7 Nd 0.3 Al 11.7 Ni 0.3 O 19 , Ca 0.6 Nd 0.4 Al 11.6 Ni 0.4 O 19 , Ca 0.5 Nd 0.5 Al 11.5 Ni 0.5 O 19 , Ca 0.4 Nd 0.6 Al 11.4 Ni 0.6 O 19 , Ca 0.3 Nd 0.7 Al 11.3 Ni 0.7 O 19 , Ca 0.2 Nd 0.8 Al 11.2 Ni 0.8 O 19 , Ca 0.1 Nd 0.9 Al 11.1 Ni 0.9 O 19 , CaAl 11.4 Nb 0.2 Ni 0.4 O 19 , CaAl 11.4 Ta 0.2 Ni 0.4 O 19 , CaAl 11.4 V 0.2 Ni 0.4 O 19 , CaAl 11.4 Sb 0.2 Ni 0.4 O 19 , CaAl 11 Zr 0.5 Ni 0.5 O 19 or CaAl 11 Te 0.5 Ni 0.5 O 19 .
5. The compound of claim 1 , wherein M a comprises Ni, Co or any combination thereof.
6. The compound of claim 1 wherein M a is Ni.
7. The compound of claim 1 , wherein x+y is less than or equal to 4.
8. The compound of claim 1 , wherein y is from 0 to 2.
9. The compound of claim 8 , wherein x is from 0.01 to 2.
10. The compound of claim 1 , wherein the compound has a blue color.
11. The compound of claim 10 , wherein the blue color has a wavelength of from about 440 nm to about 510 nm.
12. The compound of claim 10 , wherein the compound has a hibonite crystal structure.
13. The compound of claim 10 , wherein M b comprises Ti.
14. The compound of claim 10 , wherein A comprises Ca, La, Sr or any combination thereof.
15. The compound of claim 10 , wherein M a is Co and x is from 0.05 to 1.5.
16. The compound of claim 10 , wherein:
M a is Ni;
M b is selected from Ti, Ge, Sn or any combination thereof; and
x is from 0.05 to 1.5.
17. The compound of claim 1 , wherein M a comprises at least two metals selected from Ni, Cr, Cu, V, Mn, Co or Fe.
18. The compound of claim 1 , wherein M a comprises V and at least one additional metal selected from Ni, Cr, Cu, Mn, Co or Fe.
19. The compound of claim 1 , wherein M a comprises Cr and at least one additional metal selected from Ni, V, Cu, Mn, Co or Fe.
20. A composition, comprising:
a compound of claim 1 ; and
at least one additional component.
21. The composition of claim 20 , wherein the composition is a paint, an ink, a dye, a glass, a plastic, an emulsion, a fabric, or a cosmetic preparation.
22. The composition of claim 20 , wherein the at least one additional component is a binder, a solvent, a catalyst, a thickener, a stabilizer, an emulsifier, a texturizer, an adhesion promoter, a UV stabilizer, a flattener, a preservative, a polymer, a dispersion aid, a plasticizer, a flame retardant, an oxide of a metal, or any combination thereof.
23. The composition of claim 20 , wherein the composition is a glass, and the at least one additional component is a metal oxide.
24. The composition of claim 20 , further comprising at least one additional compound according to claim 1 .
25. A method for making a compound of claim 1 , the method comprising:
selecting metals desired in the compound;
providing reactants comprising the selected metals;
combining the reactants in stoichiometric amounts to achieve a desired final ratio of the selected metals in the compound; and
heating the combination of reactants at an effective temperature for an effective period of time to make the compound of claim 1 .