Lithium hydrogen titanate Li—H—Ti—O material and method for making the same

1. A lithium hydrogen titanate Li—H—Ti—O material comprising Li, H, Ti, and O elements, wherein a mass percentage of Li is in a range from about 4% to about 12%, a mass percentage of H is in a range from about 0.1% to about 5%, a mass percentage of Ti is in a range from about 48% to about 56%, and a mass percentage of O is in a range from about 28% to about 47%.

2. The lithium hydrogen titanate Li—H—Ti—O material of claim 1 , wherein some of the Li, Ti, and O elements are in forms of a plurality of Li 4 Ti 5 O 12 and TiO 2 nanostructures.

3. The lithium hydrogen titanate Li—H—Ti—O material of claim 2 , wherein the Li, Ti, O, and H elements not in forms of Li 4 Ti 5 O 12 and TiO 2 nanostructures are in a form of a layered structure material.

4. The lithium hydrogen titanate Li—H—Ti—O material of claim 3 , wherein in the layered structure material, some of the Li, Ti, and O elements are in forms of pseudohydrates.

5. The lithium hydrogen titanate Li—H—Ti—O material of claim 4 , wherein the pseudohydrates are selected from the group consisting of hydroxide ions, hydroxonium ions, —OH groups, —H groups, and combinations thereof.

6. The lithium hydrogen titanate Li—H—Ti—O material of claim 2 , wherein the plurality of Li 4 Ti 5 O 12 and TiO 2 nanostructures are uniformly and dispersingly distributed.

7. The lithium hydrogen titanate Li—H—Ti—O material of claim 2 , wherein the plurality of Li 4 Ti 5 O 12 and TiO 2 nanostructures are smaller than 10 nm.

8. The lithium hydrogen titanate Li—H—Ti—O material of claim 3 , wherein the plurality of Li 4 Ti 5 O 12 and TiO 2 nanostructures are in situ grown on the layered structure material.

9. A lithium ion battery comprising a cathode, an anode, a separator, and an electrolyte, the cathode and the anode are separated from each other by the separator, the electrolyte conducts lithium ions between the cathode and the anode, wherein the cathode or the anode comprises a lithium hydrogen titanate Li—H—Ti—O material comprising Li, H, Ti, and O elements, a mass percentage of Li is in a range from about 4% to about 12%, a mass percentage of H is in a range from about 0.1% to about 5%, a mass percentage of Ti is in a range from about 48% to about 56%, and a mass percentage of O is in a range from about 28% to about 47%.

10. A method for making a lithium hydrogen titanate Li—H—Ti—O material comprising Li, H, Ti, and O elements, wherein a mass percentage of Li is in a range from about 4% to about 12%, a mass percentage of H is in a range from about 0.1% to about 5%, a mass percentage of Ti is in a range from about 48% to about 56%, and a mass percentage of O is in a range from about 28% to about 47%, the method comprising:

preparing a titanic acid nanosized material;

mixing the titanate acid nanosized material and a lithium salt water solution into a second mixture;

stirring the second mixture for about 0.5 hours to about 4 hours to form a third precursor;

hydrothermal reacting the third precursor at a temperature of about 80° C. to about 200° C. for about 5 hours to about 72 hours to obtain a fourth precursor; and

heating the fourth precursor by elevating the temperature of the fourth precursor to a temperature of about 150° C. to about 200° C., and keeping the fourth precursor at the temperature of about 150° C. to about 200° C. for about 0.5 hours to about 5 hours to obtain a fifth precursor;

heating the fifth precursor by elevating the temperature of the fifth precursor to a temperature of about 200° C. to about 400° C., and keeping the fifth precursor at the temperature of about 200° C. to about 400° C. for about 0.5 hours to about 10 hours to form an HN material.

11. The method of claim 10 , wherein the titanic acid nanosized material is prepared by:

mixing a titanium compound and an alkaline water solution into a first mixture;

stirring the first mixture for about 3 hours to about 5 hours to form a first precursor;

hydrothermal reacting the first precursor at a temperature of about 80° C. to about 200° C. for about 4 hours to about 96 hours to obtain a second precursor; and

stirring the second precursor in a sufficient amount of an acidic water solution for about 0.5 hours to about 12 hours to form the titanic acid nanosized material.

12. The method of claim 11 , wherein the titanium compound is selected from the group consisting of anatase titanium dioxide, rutile titanium dioxide, metatitanic acid, amorphous titanium dioxide, titanate, and combinations thereof.

13. The method of claim 11 , wherein the alkaline water solution comprises an alkali selected from the group consisting of sodium hydroxide, potassium hydroxide, and combinations thereof, a concentration of the alkaline water solution is about 5 mol/L to about 20 mol/L, and a ratio between the titanium compound and the alkaline water solution is 3 g to 14 g of the titanium compound per 100 mL of the alkaline water solution.

14. The method of claim 11 , wherein the acidic water solution comprises an acid selected from the group consisting of nitric acid, hydrochloric acid, sulfuric acid, acetic acid, phosphoric acid, oxalic acid, hydrofluoric acid, and combinations thereof.