Rapid gas decompression-resistant fluoroelastomer compositions and molded articles
The disclosure herein includes rapid gas decompression (RGD)-resistant fluoroelastomeric compositions and includes a curable fluoropolymer having a curesite monomer with at least one functional group capable of curing with a peroxide curative. The compositions include a bisphenyl-based curative and an organic peroxide curative and an organic peroxide co-curative. The fluoroelastomeric compositions have a ratio of the bisphenyl-based curative to the organic peroxide co-curative of about 0.25:1 to about 1.5:1 and a ratio of the bisphenyl-based curative to the organic peroxide of about 0.5:1 to about 1.5:1. Such compositions can be formed into seals meeting RGD industry standards in a variety of sizes, up to and/or exceeding 5 mm in thickness or cross-sectional diameter.
1. A method of preparing a rapid gas decompression-resistant fluoroelastomeric composition, comprising:
providing a curable fluoropolymer comprising a curesite monomer having at least one functional group capable of curing with a peroxide curative;
combining 100 parts by weight of the curable fluoropolymer with about 1.5 to about 3 parts by weight of a bisphenyl-based curative, about 2 to about 5 parts by weight of an organic peroxide curative and about 3 to about 6 parts by weight of an organic peroxide co-curative, each based on 100 parts by weight of the curable fluoropolymer, wherein a weight ratio of the bisphenyl-based curative to the organic peroxide co-curative of about 0.25:1 to about 1.5:1 and a weight ratio of the bisphenyl-based curative to the organic peroxide curative of about 0.5:1 to about 1.5:1.
2. The method according to claim 1 , wherein the weight ratio of the bisphenyl-based curative to the organic peroxide co-curative is about 0.4:1 to about 1.2:1 and the weight ratio of the bisphenyl-based curative to the organic peroxide curative is about 0.60:1 to about 1.4:1.
3. The method according to claim 1 , wherein upon cure, the resulting cured composition exhibits no cracking meeting a rating of 0 under the test and rating method of ISO 23936-2:2011(E)-B.4.2.
4. The method according to claim 1 , wherein upon cure, the resulting cured composition is formed as a seal having a cross-sectional diameter of at least about 5.3 mm.
5. The method according to claim 4 , wherein the cross-sectional diameter is up to about 10 mm.