Transparent thermoplastic resin composition and article produced therefrom

1. A thermoplastic resin composition comprising:

a polyalkyl (meth)acrylate resin having a weight average molecular weight of about 100,000 g/mol to about 145,000 g/mol;

a rubber-modified aromatic vinyl graft copolymer; and

an aromatic vinyl resin, wherein the aromatic vinyl resin is a polymer of a monomer mixture comprising about 35 mol % to about 80 mol % of an alkyl (meth)acrylate, about 20 mol % to about 40 mol % of maleic anhydride (MAH), about 10 mol % to about 50 mol % of an aromatic vinyl monomer, and about 0.1 mol % to about 10 mol % of a vinyl cyanide monomer.

2. The thermoplastic resin composition according to claim 1 , comprising: about 30 wt % to about 85 wt % of the polyalkyl (meth)acrylate resin, about 5 wt % to about 30 wt % of the rubber-modified aromatic vinyl graft copolymer, and about 10 wt % to about 50 wt % of the aromatic vinyl resin.

3. The thermoplastic resin composition according to claim 1 , wherein the polyalkyl (meth)acrylate resin is poly(methyl methacrylate).

4. The thermoplastic resin composition according to claim 1 , wherein the polyalkyl (meth)acrylate resin has a glass transition temperature of about 110° C. or higher.

5. The thermoplastic resin composition according to claim 1 , wherein the rubber-modified aromatic vinyl graft copolymer is prepared by grafting an aromatic vinyl monomer and a monomer copolymerizable with the aromatic vinyl monomer to a rubbery polymer.

6. The thermoplastic resin composition according to claim 5 , wherein the rubbery polymer has an average particle diameter of about 0.1 μm to about 0.5 μm, and the monomer copolymerizable with the aromatic vinyl monomer comprises at least one of a vinyl cyanide monomer and an alkyl (meth)acrylic monomer.

7. The thermoplastic resin composition according to claim 1 , wherein the aromatic vinyl resin has a glass transition temperature of about 130° C. or higher.

8. The thermoplastic resin composition according to claim 1 , wherein the thermoplastic resin composition has a haze of about 2% or less and a light transmittance of about 90% or higher, as measured on an about 2.5 mm thick specimen.

9. The thermoplastic resin composition according to claim 1 , wherein the thermoplastic resin composition has a heat deflection temperature of about 100° C. to about 130° C., as measured in accordance with ASTM D648.

10. The thermoplastic resin composition according to claim 1 , wherein the thermoplastic resin composition has a scratch width of about 240 μm or less, as measured by a ball-type scratch profile test, and a pencil hardness of 2H or higher, as measured in accordance with ASTM D3362.

11. The thermoplastic resin composition according to claim 1 , wherein the thermoplastic resin composition has a notched Izod impact strength of about 5 kgf·cm/cm or higher, as measured on an about ⅛″ thick specimen in accordance with ASTM D256.

12. A molded article formed of the thermoplastic resin composition according to claim 1 .

13. The thermoplastic resin composition according to claim 1 , wherein the aromatic vinyl resin comprises about 40 mol % to about 80 mol % of the alkyl (meth)acrylate.

14. The thermoplastic resin composition according to claim 1 , wherein the aromatic vinyl resin comprises about 45 mol % to about 80 mol % of the alkyl (meth)acrylate.

15. The thermoplastic resin composition according to claim 1 , wherein the aromatic vinyl resin comprises about 50 mol % to about 80 mol % of the alkyl (meth)acrylate.

16. The thermoplastic resin composition according to claim 1 , wherein the thermoplastic resin composition has a haze of about 2% or less and a light transmittance of about 90% or higher, as measured on an about 2.5 mm thick specimen; a heat deflection temperature of about 100° C. to about 130° C., as measured in accordance with ASTM D648; a scratch width of about 240 μm or less, as measured by a ball-type scratch profile test, and a pencil hardness of 2H or higher, as measured in accordance with ASTM D3362; and a notched Izod impact strength of about 5 kgf·cm/cm or higher, as measured on an about ⅛″ thick specimen in accordance with ASTM D256.

17. The thermoplastic resin composition according to claim 16 , wherein the thermoplastic resin composition has a haze of about 0.1% to about 1.5% and a light transmittance of about 90% to about 96%, as measured on an about 2.5 mm thick specimen; a heat deflection temperature of about 100° C. to about 120° C., as measured in accordance with ASTM D648; a scratch width of about 150 μm to about 240 μm, as measured by a ball-type scratch profile test, and a pencil hardness of 2H or 3H, as measured in accordance with ASTM D3362; and a notched Izod impact strength of about 5 kgf·cm/cm to about 20 kgf·cm/cm, as measured on an about ⅛″ thick specimen in accordance with ASTM D256.

18. The molded article according to claim 12 , wherein the molded article has a haze of about 2% or less and a light transmittance of about 90% or higher, as measured on an about 2.5 mm thick specimen; a heat deflection temperature of about 100° C. to about 130° C., as measured in accordance with ASTM D648; a scratch width of about 240 μm or less, as measured by a ball-type scratch profile test, and a pencil hardness of 2H or higher, as measured in accordance with ASTM D3362; and a notched Izod impact strength of about 5 kgf·cm/cm or higher, as measured on an about ⅛″ thick specimen in accordance with ASTM D256.

19. The molded article according to claim 18 , wherein the molded article has a haze of about 0.1% to about 1.5% and a light transmittance of about 90% to about 96%, as measured on an about 2.5 mm thick specimen; a heat deflection temperature of about 100° C. to about 120° C., as measured in accordance with ASTM D648; a scratch width of about 150 μm to about 240 μm, as measured by a ball-type scratch profile test, and a pencil hardness of 2H or 3H, as measured in accordance with ASTM D3362; and a notched Izod impact strength of about 5 kgf·cm/cm to about 20 kgf·cm/cm, as measured on an about ⅛″ thick specimen in accordance with ASTM D256.