Conductive elastomer composition and molded article of the same
There is provided an elastomer composition having both of a flexibility and a wear resistance at a low temperature, while having a high conductivity, and containing an elastomer component (A) including styrene-based thermoplastic elastomer (a1) and propylene-based elastomer (a2); and containing 10 pts.mass or more and 100 pts.mass or less of a conductivity imparting agent (B), and 10 pts.mass or more and 300 pts.mass of less of a process oil (C) based on 100 pts.mass of the elastomer component (A).
1. An elastomer composition, comprising:
an elastomer component (A) consisting of styrene-based thermoplastic elastomer (a1) and propylene-based elastomer (a2);
a conductivity imparting agent (B) contained in an amount of 10 pts.mass or more and 100 pts.mass or less based on 100 pts.mass of the elastomer component (A); and
a process oil (C) contained in an amount of 10 pts.mass or more and 300 pts.mass or less based on 100 pts.mass of the elastomer component (A),
wherein only the elastomer component (A) is contained as a polymer component, and
wherein the styrene-based thermoplastic elastomer (a1) consists of a styrene-ethylene-ethylene-propylene-styrene block copolymer.
2. The elastomer composition according to claim 1 , wherein the propylene-based elastomer (a2) has a crystal fusion heat of 25 J/g or less as determined by differential scanning calorimetry.
3. The elastomer composition according to claim 1 , wherein the propylene-based elastomer (a2) has a glass transition temperature of −5° C. or less.
4. The elastomer composition according to claim 1 , wherein the elastomer component (A) contains the styrene-based thermoplastic elastomer (a1) and the propylene-based elastomer (a2) at a mass ratio in a range of 10:90 to 90:10.
5. The elastomer composition according to claim 1 , wherein the elastomer component (A) contains the styrene-based thermoplastic elastomer (a1) and the propylene-based elastomer (a2) at a mass ratio in a range of 30:70 to 80:20.
6. The elastomer composition according to claim 1 , wherein the conductivity imparting agent (B) is contained in an amount of 20 pts.mass or more and 80 pts.mass or less based on 100 pts.mass of the elastomer component (A).
7. The elastomer composition according to claim 1 , wherein the propylene-based elastomer (a2) includes a copolymer having a segment composed of propylene, and a segment composed of α-olefin.
8. The elastomer composition according to claim 1 , wherein the amount of the conductivity imparting agent (B) is in a range from 20 pts.mass to 80 pts.mass based on 100 pts.mass of the elastomer component (A).
9. The elastomer composition according to claim 1 , wherein the conductivity imparting agent (B) comprises carbon black.
10. The elastomer composition according to claim 1 , wherein the conductivity imparting agent (B) comprises Ketjen black.
11. The elastomer composition according to claim 1 , wherein the amount of the process oil (C) is in a range from 20 pts.mass to 200 pts.mass based on 100 pts.mass of the elastomer component (A).
12. A molded article composed of an elastomer composition, the elastomer composition comprising:
an elastomer component (A) consisting of styrene-based thermoplastic elastomer (a1) and propylene-based elastomer (a2);
a conductivity imparting agent (B) contained in an amount of 10 pts.mass or more and 100 pts.mass or less based on 100 pts.mass of the elastomer component (A); and
a process oil (C) contained in an amount of 10 pts.mass or more and 300 pts.mass or less based on 100 pts.mass of the elastomer component (A),
wherein only the elastomer component (A) is contained as a polymer component, and
wherein the stryene-based thermoplastic elastomer (a1) consists of a styrene-ethylene-ethylene-propylene-styrene block copolymer.
13. The molded article according to claim 12 , wherein a storage elastic modulus at −10° C. is 500 MPa or less, and a volume resistivity is 1 Ω·cm or less.
14. The molded article according to claim 12 , wherein the elastomer composition is formed by dynamic crosslinking, and a crosslinked structure is introduced to the styrene-based thermoplastic elastomer (a1).
15. The molded article according to claim 12 , is formed into a sheet shape, and is formed as at least one of an electromagnetic shielding, an anti-static material, and a pressure-sensitive switch electrode.
16. The molded article according to claim 12 , wherein the amount of the conductivity imparting agent (B) is in a range from 20 pts.mass to 80 pts.mass based on 100 pts.mass of the elastomer component (A).
17. The molded article according to claim 12 , wherein the conductivity imparting agent (B) comprises carbon black.
18. The molded article according to claim 12 , wherein the conductivity imparting agent (B) comprises Ketjen black.
19. The molded article according to claim 12 , wherein the amount of the process oil (C) is in a range from 20 pts.mass to 200 pts.mass based on 100 pts.mass of the elastomer component (A).