Method for making colored film, colored film, colored material, and ophthalmic lens

1. A method for making a colored film, comprising:

providing a mixture comprising a hydrophilic monomer, a functionalized vinylic monomer, a clay, a cross-linking agent, and an initiator;

mixing a pigment and a solvent with the mixture to form a colored material; and

placing the colored material into a mold, and exposing the colored material to ultraviolet radiation or heating the colored material, to cause the hydrophilic monomer, the functionalized vinylic monomer, the cross-linking agent, and the initiator in the colored material to undergo a polymerization reaction to form a cross-linking network, and the clay in the colored material to be dispersed in the cross-linking network, thereby forming the colored film;

wherein the hydrophilic monomer has a mass percentage of about 20% to about 50% of a total mass of the mixture, the functionalized vinylic monomer has a mass percentage of about 25% to about 60% of the total mass of the mixture, the clay has a mass percentage of about 0.5% to about 42% of the total mass of the mixture, the cross-linking agent has a mass percentage of about 1% to about 25% of the total mass of the mixture, the initiator has a mass percentage of about 0.5% to about 20% of the total mass of the mixture, the mixture has a mass percentage of about 40% to about 75% of the total mass of the colored material, the pigment has a mass percentage of about 10% to about 55% of the total mass of the colored material, the solvent has a mass percentage of about 1% to about 20% of the total mass of the colored material.

2. The method of claim 1 , wherein the clay comprises aluminium silicate.

3. The method of claim 1 , wherein the functionalized vinylic monomer comprises at least one functional group selected from a group consisting of hydroxyl group, amino group, imino group, carboxyl group, epoxy group, amide group, acyl halogeno group, isothiocyanate group, isocyanate group, halogeno group, and acid anhydride.

4. The method of claim 1 , wherein the solvent is water or an organic solvent.

5. A colored material comprising:

a pigment;

a solvent; and

a mixture comprising a hydrophilic monomer, a functionalized vinylic monomer, a clay, a cross-linking agent, and an initiator;

wherein the hydrophilic monomer has a mass percentage of about 20% to about 50% of a total mass of the mixture, the functionalized vinylic monomer has a mass percentage of about 25% to about 60% of the total mass of the mixture, the clay has a mass percentage of about 0.5% to about 42% of the total mass of the mixture, the cross-linking agent has a mass percentage of about 1% to about 25% of the total mass of the mixture, the initiator has a mass percentage of about 0.5% to about 20% of the total mass of the mixture, the mixture has a mass percentage of about 40% to about 75% of the total mass of the colored material, the pigment has a mass percentage of about 10% to about 55% of the total mass of the colored material, the solvent has a mass percentage of about 1% to about 20% of the total mass of the colored material.

6. The colored material of claim 5 , wherein the clay comprises aluminium silicate.

7. The colored material of claim 5 , wherein the functionalized vinylic monomer comprises at least one functional group selected from a group consisting of hydroxyl group, amino group, imino group, carboxyl group, epoxy group, amide group, acyl halogeno group, isothiocyanate group, isocyanate group, halogeno group, and acid anhydride.

8. The colored material of claim 5 , wherein the solvent is water or an organic solvent.

9. A colored film comprising:

a cross-linking network; and

a clay dispersed in the cross-linking network;

wherein the cross-linking network is formed by providing a colored material comprising a pigment, a solvent, and a mixture of a hydrophilic monomer, a functionalized vinylic monomer, a clay, a cross-linking agent, and an initiator, and exposing the colored material to ultraviolet radiation or heating the colored material, to cause the hydrophilic monomer, the functionalized vinylic monomer, the cross-linking agent, and the initiator to undergo a polymerization reaction; the hydrophilic monomer has a mass percentage of about 20% to about 50% of a total mass of the mixture, the functionalized vinylic monomer has a mass percentage of about 25% to about 60% of the total mass of the mixture, the clay has a mass percentage of about 0.5% to about 42% of the total mass of the mixture, the cross-linking agent has a mass percentage of about 1% to about 25% of the total mass of the mixture, the initiator has a mass percentage of about 0.5% to about 20% of the total mass of the mixture, the mixture has a mass percentage of about 40% to about 75% of the total mass of the colored material, the pigment has a mass percentage of about 10% to about 55% of the total mass of the colored material, the solvent has a mass percentage of about 1% to about 20% of the total mass of the colored material.

10. The colored film of claim 9 , wherein the clay comprises aluminium silicate.

11. The colored film of claim 9 , wherein the functionalized vinylic monomer comprises at least one functional group selected from a group consisting of hydroxyl group, amino group, imino group, carboxyl group, epoxy group, amide group, acyl halogeno group, isothiocyanate group, isocyanate group, halogeno group, and acid anhydride.

12. An ophthalmic lens comprising:

a lens substrate comprising a transparent pupil region and a substantially annular iris region surrounding the pupil region; and

a colored film attached to a surface of the iris region;

wherein the colored film comprises a cross-linking network, and a clay is dispersed in the cross-linking network, the cross-linking network is formed by providing a colored material comprising a pigment, a solvent, and a mixture of a hydrophilic monomer, a functionalized vinylic monomer, a clay, a cross-linking agent, and an initiator, and exposing the colored material to ultraviolet radiation or heating the colored material, to cause the hydrophilic monomer, the functionalized vinylic monomer, the cross-linking agent, and the initiator to undergo a polymerization reaction.

13. The ophthalmic lens of claim 12 , wherein the clay comprises aluminium silicate.

14. The ophthalmic lens of claim 13 , wherein the hydrophilic monomer has a mass percentage of about 20% to about 50% of a total mass of the mixture, the functionalized vinylic monomer has a mass percentage of about 25% to about 60% of the total mass of the mixture, the clay has a mass percentage of about 0.5% to about 42% of the total mass of the mixture, the cross-linking agent has a mass percentage of about 1% to about 25% of the total mass of the mixture, the initiator has a mass percentage of about 0.5% to about 20% of the total mass of the mixture, the mixture has a mass percentage of about 40% to about 75% of the total mass of the colored material, the pigment has a mass percentage of about 10% to about 55% of the total mass of the colored material, the solvent has a mass percentage of about 1% to about 20% of the total mass of the colored material.

15. The ophthalmic lens of claim 13 , wherein the functionalized vinylic monomer comprises at least one functional group selected from a group consisting of hydroxyl group, amino group, imino group, carboxyl group, epoxy group, amide group, acyl halogeno group, isothiocyanate group, isocyanate group, halogeno group, and acid anhydride.

16. The ophthalmic lens of claim 13 , wherein the lens substrate further comprises the clay.