Degradable conjugated polymers for the selective sorting of semiconducting carbon nanotubes
Conjugated polymers composed of bi-pyridine units linked to 9,9-dialkyl fluorenyl-2,7-diyl units via imine linkages along the polymer backbone are provided. Also provided are semiconducting single-walled carbon nanotubes coated with the conjugated polymers and methods of sorting and separating s-SWCNTs from a sample comprising a mixture of s-SWCNTs and metallic single-walled carbon nanotubes using the conjugated polymers.
1. A conjugated polymer having the structure:
where R represents a functional group comprising an alkyl chain and n represents the number of repeat units in the conjugated polymer.
2. The conjugated polymer of claim 1 , wherein R has the structure: C x H (2x+1) , where x is in the range from 6 to 30.
3. Polymer-wrapped semiconducting single-walled carbon nanotubes comprising semiconducting single-walled carbon nanotubes coated by a conjugated polymer having the structure:
where R represents a functional group comprising an alkyl chain and n represents the number of repeat units in the conjugated polymer.
4. The polymer-wrapped semiconducting single-walled carbon nanotubes of claim 3 , wherein n has a value of 15 or lower.
5. The polymer-wrapped semiconducting single-walled carbon nanotubes of claim 3 , wherein R has the structure: C x H (2x+1) , where x is in the range from 6 to 20.
6. A method of separating semiconducting single-walled carbon nanotubes from a starting carbon nanotube sample comprising a mixture of semiconducting single-walled carbon nanotubes and metallic single-walled carbon nanotubes, the method comprising:
forming a solution comprising the carbon nanotube sample and a conjugated polymer having the structure:
where R represents a functional group comprising an alkyl chain and n represents the number of repeat units in the conjugated polymer, wherein the conjugated polymer preferentially coats and disperses the semiconducting single-walled carbon nanotubes, relative to the metallic single-walled carbon nanotubes, in the solution; and
separating the dispersed single-walled carbon nanotubes from the undispersed single-walled carbon nanotubes to obtain a purified carbon nanotube sample, wherein the purified carbon nanotube sample has a higher ratio of semiconducting single-walled carbon nanotubes to metallic single-walled carbon nanotubes than did the starting carbon nanotube sample.
7. The method of claim 6 , wherein n has a value of 15 or lower.
8. The method of claim 6 , wherein n has a value of 10 or lower.
9. The method of claim 6 , wherein the purified carbon nanotube sample comprises at least 99% semiconducting single-walled carbon nanotubes, based on the total number of semiconducting single-walled carbon nanotubes and metallic single-walled carbon nanotubes.
10. The method of claim 6 , further comprising removing the coating of the conjugated polymer from the semiconducting single-walled carbon nanotubes in the purified carbon nanotube sample.
11. The method of claim 10 , wherein removing the coating of the conjugated polymer from the semiconducting single-walled carbon nanotubes comprises depolymerizing the conjugated polymer with acid, heat, or a combination of acid and heat.
12. The method of claim 11 , wherein removing the coating of the conjugated polymer from the semiconducting single-walled carbon nanotubes comprises depolymerizing the conjugated polymer with acid.
13. The method of claim 11 , wherein removing the coating of the conjugated polymer from the semiconducting single-walled carbon nanotubes comprises depolymerizing the conjugated polymer with heat.
14. The method of claim 6 , where R has the structure: C x H (2x+1) , where x is in the range from 6 to 20.
15. A method of separating semiconducting single-walled carbon nanotubes from a starting carbon nanotube sample comprising a mixture of semiconducting single-walled carbon nanotubes and metallic single-walled carbon nanotubes, the method comprising:
forming a solution comprising the carbon nanotube sample and a conjugated polymer having imine linkages along its polymer backbone chain, wherein the conjugated polymer preferentially coats and disperses the semiconducting single-walled carbon nanotubes, relative to the metallic single-walled carbon nanotubes, in the solution;
separating the dispersed single-walled carbon nanotubes from the undispersed single-walled carbon nanotubes to obtain a purified carbon nanotube sample, wherein the purified carbon nanotube sample has a higher ratio of semiconducting single-walled carbon nanotubes to metallic single-walled carbon nanotubes than did the starting carbon nanotube sample; and
heating the conjugated polymer-coated semiconducting single-walled carbon nanotubes to a temperature at which the backbone of the conjugated polymer thermally decomposes, whereby at least 60 percent, by weight, of the coating of the conjugated polymer is removed from the semiconducting single-walled carbon nanotubes.
16. The method of claim 15 , wherein the thermal decomposition of the conjugated polymer is carried out in the absence of acid.
17. The method of claim 15 , wherein the thermal decomposition of the conjugated polymer is carried out at a temperature in range from 300° C. to 500° C.