Method for producing an insulating composite building block
A method for producing a composite insulating mineral block, includes providing a mineral masonry block including at least one cell with walls having a water absorption rate of less than 5 g/(m 2 ·s) at 10 minutes, and filling the cell with a mineral cement foam, wherein a cement used to produce the mineral cement foam has an aluminum oxide content of less than 20% by weight of the cement.
1. A method for producing a composite insulating mineral block, comprising the following steps:
a) providing a mineral masonry block comprising at least one cell with walls having a water absorption rate of less than 5 g/(m 2 ·s) at 10 minutes, and
b) filling said cell with a mineral cement foam, wherein a cement used to produce said mineral cement foam has an aluminium oxide content of less than 20% by weight of the cement.
2. The method according to claim 1 , wherein the block used at step a) is in a fresh state or sufficiently wet.
3. The method according to claim 1 , wherein the mineral cement foam does not comprise any quick-setting cement.
4. The method according to claim 1 , wherein the mineral cement foam has a density of less than 600 kg/m 3 .
5. The method according to claim 1 , wherein the mineral cement foam used at step b) has thermal conductivity ranging from 0.03 to 0.06 W/m·K.
6. The method according to claim 1 , wherein said cell is a through cell.
7. The method according to claim 1 , wherein the block is a concrete block.
8. The method according to claim 1 , wherein a time lapse between steps a) and b) does not exceed 60 minutes.
9. The method according to claim 8 , wherein the time lapse between steps a) and b) does not exceed 30 minutes.
10. The method according to claim 1 , further comprising a step for applying a water repellent compound to the cell walls of the block, a preliminary step before filling step b).
11. The method according claim 1 , wherein the block used at step a) comprises a water repellent compound mixed in the bulk of the block.
12. The method according to claim 1 , wherein the method is performed without carrying out a drying or oven baking step of the block before steps a) or b).
13. The method according to claim 1 , wherein the method is a continuous or semi-continuous method.
14. A composite insulating mineral block obtained by the method according to claim 1 .
15. A method comprising building a structure with a composite insulating mineral block according to claim 14 .
16. The method according to claim 15 , wherein the composite insulating mineral block is arranged in said structure by masonry.