Polyester film and manufacturing method therefor, and polyester mold product using same and manufacturing method therefor
Provided are a polyester film that is usable for protecting a surface of a metal plate of a construction material, a decorative material, an interior material, an electronic product, etc., and a manufacturing method therefor, and a polyester mold product using the same and a manufacturing method therefor, wherein the polyester film has low orientation and low modulus to have excellent moldability.
1. A polyester film consisting of a copolymerized polyester alone or a mixture of a copolymerized polyester and a homo polyethylene terephthalate resin,
wherein 20% tensile modulus F20 is 8.0 to 14.5 kg/mm 2 , and 100% tensile modulus F100 is 11.0 to 21.5 kg/mm 2 in a machine direction and a transverse direction,
a modulus variation A according to a tensile rate according to Equation 1 below in 20% to 100% of tensile section is 3 to 10 kg/mm 2 :
A =( F 100− F 20)/0.8, [Equation 1]
a heat shrinkage of the film in the machine direction and the transverse direction after heat treatment at 150° C. for 30 minutes is 2% or less, and
moldability is 80% or more, and
wherein the polyester film includes 1 to 4.8 mol % of neopentyl glycol unit, based on a total moles of diol components in the polyester film, and
wherein the copolymerized polyester consists of a terephthalic acid unit, an ethylene glycol unit and the neopentyl glycol unit.
2. The polyester film of claim 1 , wherein shrinkage stress in the machine direction after 100 seconds at 140° C. from an initial load of 6.21 N/mm 2 is −5.5 to −3.0 N/mm 2 , and shrinkage stress in the machine direction after 100 seconds at 140° C. from an initial load of 0.65 N/mm 2 is −0.5 to 1.0 N/mm 2 .
3. The polyester film of claim 1 , wherein the polyester film has a melting point of 240 to 253° C.
4. The polyester film of claim 1 , wherein the polyester film has a plane orientation coefficient of 0.120 to 0.155.
5. The polyester film of claim 1 , wherein the polyester film has density of 1.384 to 1.397 g/cm 3 .
6. The polyester film of claim 1 , wherein the polyester film has a total thickness of 10 to 100 μm.
7. The polyester film of claim 1 , wherein the polyester film has a surface concave-convex formed on at least any one surface by hair-line processing.