Stabilizer bar with rubber bush and method for producing same
A stabilizer bar with rubber bush includes a stabilizer bar ( 2 ), and at least one rubber bush ( 6 ) adhesively fixed to at least a portion of the stabilizer bar. The stabilizer bar ( 2 ) and the rubber bush ( 6 ) are adhesively fixed to each other with an adhesive agent layer ( 3 ). The adhesive agent layer ( 3 ) includes a primer agent layer ( 4 ) formed on a surface of the stabilizer bar ( 2 ) and having a dry film thickness of 3 μm or more and 13 μm or less; and a first top coat agent layer ( 5 ) formed on the primer agent layer ( 4 ) and having a dry film thickness of 5 μm or more and less than 13 μm.
1. A method for producing a stabilizer bar with rubber bush, comprising:
a rubber bush-cleaning step of ultrasonically cleaning a rubber bush in hot water;
a primer agent layer formation step of forming a primer agent layer by applying a primer agent to a stabilizer bar at a predetermined portion where the rubber bush is to be adhered to achieve a dry film thickness of 3 μm or more and 13 μm or less, followed by drying;
a first top coat agent layer formation step of forming a first top coat agent layer by applying a first top coat agent onto the formed primer agent layer to achieve a dry film thickness of 5 μm or more and less than 13 μm, followed by drying; and
an adhesive fixing step of bringing the rubber bush subjected to the ultrasonic cleaning into contact with the first top coat agent layer and adhesively fixing the rubber bush onto the first top coat agent layer,
wherein the primer agent contains a rubber resin at a ratio of 5% by mass or higher and lower than 10% by mass, and
wherein the first top coat agent contains a rubber resin at a ratio of 10% by mass or higher and 15% by mass or lower.
2. The method for producing the stabilizer bar with rubber bush set forth in claim 1 ,
wherein the rubber bush-cleaning step, the primer agent layer formation step, and the first top coat agent layer formation step are performed in an order of the primer agent layer formation step, the first top coat agent layer formation step, and the rubber bush-cleaning step or in an order of the primer agent layer formation step, the rubber bush-cleaning step, and the first top coat agent layer formation step.
3. The method for producing the stabilizer bar with rubber bush set forth in claim 1 , further comprising:
a stabilizer bar-cleaning step, before the primer agent layer formation step, of cleaning a surface of the stabilizer bar.
4. The method for producing the stabilizer bar with rubber bush set forth in claim 3 , further comprising:
a preheating step, after the stabilizer bar cleaning step, of preheating the cleaned stabilizer bar.
5. The method for producing the stabilizer bar with rubber bush set forth in claim 1 ,
wherein the hot water has a temperature of 40° C. or above and 60° C. or below, and
wherein the ultrasonic for the ultrasonic cleaning has a frequency of 25 kHz or higher and 45 kHz or lower.
6. The method for producing the stabilizer bar with rubber bush set forth in claim 1 ,
wherein the hot water has a temperature of approximately 50° C., and
wherein the ultrasonic for the ultrasonic cleaning has a frequency of approximately 38 kHz.